ULTRASTRUCTURAL-CHANGES OF PHOTODEGRADATION OF WOOD SURFACES EXPOSED TO UV

Red pine sapwood transverse and radial surfaces were exposed to ultraviolet (UV) light for 3 to 40 days. Effect of UV irradiation on ultrastructural changes of cell walls were studied by scanning (SEM) and transmission (TEM) electron microscopy. SEM study of transverse sections showed that during initial stages of UV irradiation, lignin in cell corners and in the compound middle lamellae was preferentially degraded and that the radial middle lamellae substained a greater rate of UV degradation than did the tangential middle lamellae. Massive cell wall degradation, as indicated by cell wall thinning, did not occur until surfaces were exposed to UV light for more than 10 days. TEM study of radial cell wall surfaces indicated that lignin lining the warty layer was removed by UV irradiation in 3 days and that warts were destroyed by a UV irradiation in 7 days. UV irradiation of cell wall surfaces produced a substantial amount of water-soluble degradation products. After 30 days of UV irradiation, the S3 layer was totally removed and revealed the very fragile S2 layer.