STRUCTURAL STUDY OF A HOLLANDITE-TYPE KXIRO2

被引:18
作者
BESTAOUI, N
DENIARD, P
BREC, R
机构
[1] Laboratoire de Chimie des Solides, IMN (CNRS), 44072 Nantes Cedex 03
关键词
D O I
10.1006/jssc.1995.1356
中图分类号
O61 [无机化学];
学科分类号
070301 ; 081704 ;
摘要
The new ternary oxide KxIrO2(x approximate to 0.25) was prepared by heating stoichiometric proportions of K2CO3 and pure, chlorine-free IrO2 at 1000 degrees C for 1 hr. The monoclinic cell of the phase corresponds to the following parameters: a = 10.0206(4) Angstrom, b = 3.15268(9) Angstrom, c = 10.0535(4) Angstrom, and beta = 90.113(3)degrees. The Rietveld atomic structure refinement made in the I2/m space group yielded a reliability factor of R(wp) = 17.0 and chi(2) = 1.19. The structure corresponds to a slight distortion of the well-known hollandite-type structure, with a mean Ir-O distance of 2.03 Angstrom, a value intermediary between that found for Ir(III) and Ir(IV), in agreement with partially reduced iridium in KxIrO2. (C) 1995 Academic Press, Inc.
引用
收藏
页码:372 / 377
页数:6
相关论文
共 11 条
[1]   MAXIMUM-LIKELIHOOD METHODS IN POWDER DIFFRACTION REFINEMENTS [J].
ANTONIADIS, A ;
BERRUYER, J ;
FILHOL, A .
ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 1990, 46 :692-711
[2]   STRUCTURAL AND ANALYTICAL CHARACTERIZATION OF AN IRIDIUM OXIDE THIN-LAYER [J].
BESTAOUI, N ;
PROUZET, E ;
DENIARD, P ;
BREC, R .
THIN SOLID FILMS, 1993, 235 (1-2) :35-42
[3]  
BESTAOUI N, Patent No. 9409773
[4]  
DENIARD P, 1991, MATER SCI FORUM, V363, P79
[5]   POTENTIAL OF THE INEL X-RAY POSITION-SENSITIVE DETECTOR - A GENERAL STUDY OF THE DEBYE-SCHERRER SETTING [J].
EVAIN, M ;
DENIARD, P ;
JOUANNEAUX, A ;
BREC, R .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1993, 26 :563-569
[6]  
FAUCHON E, 1987, THESIS U GRENOBLE GR
[7]  
RODRIGUEZCARJAV.J, 1992, FULLPROOF MANUAL
[8]   EFFECTIVE IONIC RADII IN OXIDES AND FLUORIDES [J].
SHANNON, RD ;
PREWITT, CT .
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL CRYSTALLOGRAPHY AND CRYSTAL CHEMISTRY, 1969, B 25 :925-&
[9]   THE STRUCTURE AND CHEMISTRY OF A BARIUM-TITANATE HOLLANDITE-TYPE PHASE [J].
SINCLAIR, W ;
MCLAUGHLIN, GM ;
RINGWOOD, AE .
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL SCIENCE, 1980, 36 (DEC) :2913-2918
[10]   SYNTHESIS AND CRYSTAL-STRUCTURE OF BARU6O12 - AN ORDERED STOICHIOMETRIC HOLLANDITE [J].
TORARDI, CC .
MATERIALS RESEARCH BULLETIN, 1985, 20 (06) :705-713