EFFECT OF CRYSTALLINE RELAXATION ON FATIGUE BEHAVIOR OF THE ORIENTED HIGH-DENSITY POLYETHYLENE BASED ON NONLINEAR VISCOELASTIC MEASUREMENTS

被引:12
作者
JO, NJ [1 ]
TAKAHARA, A [1 ]
KAJIYAMA, T [1 ]
机构
[1] KYUSHU UNIV,FAC ENGN,DEPT CHEM SCI & TECHNOL,6-10-1 HAOKOZAKI,HIGASHI KU,FUKUOKA 812,JAPAN
关键词
ORIENTED HIGH-DENSITY POLYETHYLENE; NONLINEAR VISCOELASTICITY; FATIGUE; NONLINEAR VISCOELASTIC PARAMETER; HIGHER-ORDER STRUCTURAL CHANGE; MECHANICAL CRYSTALLINE RELAXATION;
D O I
10.1295/polymj.26.1027
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Oriented high-density polyethylene (HDPE) specimens were prepared by drawing the HDPE film up to the draw ratio of 5.3 at 353 K corresponding to the crystalline relaxation temperature. Nonlinear viscoelasticity and higher-order structural change of the oriented HDPE during the fatigue process were investigated at various ambient temperatures. Nonlinear viscoelasticity of the oriented HDPE was estimated on the basis of nonlinear viscoelastic parameter (NVP). The magnitude of NVP at the alpha1-crystalline relaxation (intermosaic block crystalline relaxation) temperature region was lower than that at room temperature, since deformation in the intermosaic block region preferentially occurred in addition to that in the amorphous region. However, the fatigue strength at the alpha1-crystalline relaxation temperature was lower than that at the other ambient temperatures, because deformation in the intermosaic block region was very sensitive to strain or stress concentration. Since both lamellar crystalline and amorphous regions were deformed at the alpha2-crystalline relaxation temperature region, the magnitude of NVP became lower than that at the alpha1-crystalline relaxation temperature. Also, the fatigue strength at the alpha2-crystalline relaxation temperature was greater than that at the alpha1-crystalline relaxation temperature due to a more homogeneous deformation of the specimen.
引用
收藏
页码:1027 / 1036
页数:10
相关论文
共 15 条
[1]  
HOSEMANN R, 1968, MAKROMOL CHEM, V118, P230
[2]   DRAWING OF SINGLE-CRYSTAL MATS OF LINEAR POLYETHYLENE [J].
ISHIKAWA, K ;
MIYASAKA, K ;
MAEDA, M .
JOURNAL OF POLYMER SCIENCE PART A-2-POLYMER PHYSICS, 1969, 7 (12PA) :2029-&
[3]   ANALYSIS OF FATIGUE BEHAVIOR OF HIGH-DENSITY POLYETHYLENE BASED ON NONLINEAR VISCOELASTIC MEASUREMENT UNDER CYCLIC FATIGUE [J].
JO, NJ ;
TAKAHARA, A ;
KAJIYAMA, T .
POLYMER JOURNAL, 1993, 25 (07) :721-729
[4]   FATIGUE BEHAVIOR OF ORIENTED ULTRA-HIGH-MOLECULAR-WEIGHT POLYETHYLENE PREPARED BY GEL DRAWING [J].
KAIYA, N ;
TAKAHARA, A ;
KAJIYAMA, T .
POLYMER JOURNAL, 1990, 22 (10) :859-865
[5]   FATIGUE FRACTURE-BEHAVIOR OF SOLID-STATE EXTRUDED HIGH-DENSITY POLYETHYLENE [J].
KAIYA, N ;
TAKAHARA, A ;
KAJIYAMA, T .
POLYMER JOURNAL, 1989, 21 (07) :523-531
[6]  
KAIYA N, 1986, SEN-I GAKKAISHI, V42, pT127
[7]   ANALYSIS OF ALPHA-RELAXATION PROCESS OF BULK CRYSTALLIZED POLYETHYLENE BASED ON THAT OF SINGLE-CRYSTAL MAT [J].
KAJIYAMA, T ;
OKADA, T ;
SAKODA, A ;
TAKAYANA.M .
JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1973, B 7 (03) :583-608
[8]   MORPHOLOGICAL CHANGES, MOLECULAR CHAIN ORIENTATION, AND VISCOELASTIC PROPERTIES RELATED WITH MOSAIC BLOCK STRUCTURE OF BULK-CRYSTALLIZED POLYETHYLENE [J].
KAJIYAMA, T ;
TAKAYANA.M .
JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1974, B 10 (01) :131-155
[9]   ROLE OF MOSAIC BLOCK STRUCTURE ON ONSET OF DEFORMATION AND FATIGUE OF BULK CRYSTALLIZED POLYETHYLENE [J].
KAJIYAMA, T ;
OKADA, T ;
TAKAYANA.M .
JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1974, B 9 (01) :35-69
[10]   PLASTIC DEFORMATION OF POLYETHYLENE .2. CHANGE OF MECHANICAL PROPERTIES DURING DRAWING [J].
MEINEL, G ;
PETERLIN, A .
JOURNAL OF POLYMER SCIENCE PART A-2-POLYMER PHYSICS, 1971, 9 (01) :67-&