ELEVATED-TEMPERATURE SLOW PLASTIC-DEFORMATION OF NIAL-TIB2 PARTICULATE COMPOSITES AT 1200-K AND 1300-K

被引：94

作者：

WHITTENBERGER, JD ^{[1
]}

VISWANADHAM, RK ^{[1
]}

MANNAN, SK ^{[1
]}

SPRISSLER, B ^{[1
]}

机构：

[1] MARTIN MARIETTA CORP,BALTIMORE,MD 21227

来源：

JOURNAL OF MATERIALS SCIENCE | 1990年 / 25卷 / 1A期

关键词：

D O I：

10.1007/BF00544181

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Elevated temperature compression testing has been conducted in air at 1200 and 1300K with strain rates varying from ∼10-4 to ∼10-7sec-1 on NiAl-TiB2 particulate composites. These materials, which consisted of a B2 crystal structure intermetallic Ni-50at% Al matrix and from 0 to 30 vol % of approximately 1 μm diameter TiB2 particles, were fabricated by XD synthesis and hot pressed to full density. Flow strength of the composites increased with volume fraction of the strengthening phase with NiAl-30TiB2 being approximately three times stronger than NiAl. Comparison of the light optical and transmission electron microstructures of asreceived and tested samples revealed that reactions did not occur between the two phases, and NiAl-TiB2 interfaces were not cracked during deformation. Additional transmission electron microscopy indicated that the particles stabilize a vastly different microstructure in the NiAl matrix of the composites than that formed in unreinforced NiAl. © 1990 Chapman and Hall Ltd.

引用

页码：35 / 44

页数：10

共 26 条

[1] EFFECT OF DISLOCATION SELF-INTERACTION ON OROWAN STRESS [J].

BACON, DJ ;

KOCKS, UF ;

SCATTERGOOD, RO .

PHILOSOPHICAL MAGAZINE, 1973, 28 (06) :1241-1263

[2] DEFORMATION PROPERTIES AND ELECTRON MICROSCOPY STUDIES OF INTERMETALLIC COMPOUND NIAL [J].

BALL, A ;

SMALLMAN, RE .

ACTA METALLURGICA, 1966, 14 (10) :1349-&

[3]

BARRETT CA, UNPUB OX METALS

[4]

BROUSSAUD D, 1974, MODERN DEV POWDER ME, P589

[5]

Brown L. M., 1982, FATIGUE CREEP COMPOS, P1

[6]

Clark R. W., 1984, THERMAL EXPANSION, V8, P189

[7]

HARMOUCHE MR, 1987, J TEST EVAL, V15, P101, DOI 10.1520/JTE10989J

[8]

HOCKING LA, 1971, J I MET, V99, P98

[9] HIGH-TEMPERATURE CREEP OF NI-20CR-2THO-2 SINGLE-CRYSTALS [J].

LUND, RW ;

NIX, WD .

ACTA METALLURGICA, 1976, 24 (05) :469-481

[10] A COMPILATION AND ANALYSIS OF DATA FOR THE STRESS DEPENDENCE OF THE SUBGRAIN SIZE [J].

RAJ, SV ;

PHARR, GM .

MATERIALS SCIENCE AND ENGINEERING, 1986, 81 (1-2) :217-237

← 1 2 3 →