FAILURE OF GLASS WITH SUBTHRESHOLD FLAWS

被引：29

作者：

CHOI, SR

RITTER, JE

JAKUS, K

机构：

[1] Mechanical Engineering Department, University of Massachusetts, Amherst, Massachusetts

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 1990年 / 73卷 / 02期

关键词：

cracking; failure; flaws; glass; mechanical properties;

D O I：

10.1111/j.1151-2916.1990.tb06505.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Conventional postthreshold crack analysis cannot be used to predict the strength and fatigue behavior of glass with subthreshold flaws. Therefore, a fracture mechanics model for failure of glass with subthreshold indentation flaws was developed. This model accounts for both the near‐ and farfield residual stresses associated with the indentation impression. It is shown that these stresses play a major role in the initiation and subsequent propagation of cracks that eventually cause failure. The model predicts “pop‐in” of a well‐developed crack and failure under continuous and discontinuous crack growth in both inert and fatigue conditions. The results of experiments with bare fused silica fibers with indentation subthreshold flaws in inert and fatigue (water) environments were in good agreement with the predictions by the model. Copyright © 1990, Wiley Blackwell. All rights reserved

引用

页码：268 / 274

页数：7

共 13 条

[1] THE RESPONSE OF SOLIDS TO ELASTIC PLASTIC INDENTATION .1. STRESSES AND RESIDUAL-STRESSES [J].