ENHANCED FATIGUE-CRACK GROWTH RESISTANCE AT ELEVATED-TEMPERATURE IN TIC/TI-6AL-4V COMPOSITE - MICROCRACK-INDUCED CRACK CLOSURE

被引：19

作者：

LIU, G

ZHU, D

SHANG, JK

机构：

[1] Department of Materials Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, 61801, IL

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1995年 / 26卷 / 01期

关键词：

D O I：

10.1007/BF02669801

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The fatigue crack growth behavior of TiC/Ti-alloy composite was examined at 450 degrees C and compared to the room-temperature behavior. Contrary to the temperature-dependent fatigue crack growth behavior of the monolithic alloy, fatigue crack growth resistance of the composite was improved at the elevated temperature. At 450 degrees C, the fatigue threshold of the composite was found to be 50 pet higher than at room temperature. Such an improved fatigue crack growth resistance is shown to result from extensive microcracking of reinforcing particles, which promotes fatigue crack closure at the elevated temperature.

引用

页码：159 / 166

页数：8

共 25 条

[1]

ABKOWITZ S, 1989, ADV MATER PROCESS, V136, P31

[2] THERMAL RESIDUAL-STRESS IN METAL MATRIX COMPOSITE [J].

ARSENAULT, RJ ;

TAYA, M .

ACTA METALLURGICA, 1987, 35 (03) :651-659

[3]

CHESNUTT JC, 1978, AFMLTR7868 AIR FORC

[4]

Elber W., 1970, Engineering Fracture Mechanics, V2, P37, DOI 10.1016/0013-7944(70)90028-7

[5] FATIGUE CRACK-PROPAGATION AT ELEVATED-TEMPERATURES IN SOLID-SOLUTION STRENGTHENED SUPER-ALLOYS [J].

JABLONSKI, DA ;

CARISELLA, JV ;

PELLOUX, RM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (12) :1893-1900

[6] EFFECT OF TEMPERATURE UPON FATIGUE-CRACK GROWTH BEHAVIOR OF 2 NICKEL-BASE ALLOYS [J].

JAMES, LA .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1973, 95 (04) :254-256

[7]

KNOWLES DM, 1992, MATER SCI TECH SER, V8, P500, DOI 10.1179/026708392790170946

[8] MICROSTRUCTURAL ASSESSMENT OF TI6A14V-TIC METAL MATRIX COMPOSITE [J].

KONITZER, DG ;

LORETTO, MH .

ACTA METALLURGICA, 1989, 37 (02) :397-406

[9] INFLUENCE OF SIC PARTICLE DISTRIBUTION AND PRESTRAINING ON FATIGUE CRACK-GROWTH RATES IN ALUMINUM AA 6061-SIC COMPOSITE-MATERIAL [J].

LEVIN, M ;

KARLSSON, B .

MATERIALS SCIENCE AND TECHNOLOGY, 1991, 7 (07) :596-607

[10] TEMPERATURE-DEPENDENCE OF FRACTURE-TOUGHNESS IN TIC-PARTICULATE REINFORCED TI-6AL-4V MATRIX COMPOSITE [J].

LIU, G ;

ZHU, D ;

SHANG, JK .

SCRIPTA METALLURGICA ET MATERIALIA, 1993, 28 (06) :729-732

← 1 2 3 →