HOT PRESSED GDIG FOR MAGNETOOPTIC MEMORY APPLICATION

This paper describes the preparation of polycrystalline GdIG by hot pressing and reports the most relevant properties of the material. Hot pressed samples were prepared using various conditions of time (1 to 20 hours), temperature (900 to 1300°C) and pressure (300 to 1000 kg/cm2). Dense specimens with grain diameter ranging from 1 to 10 pm were prepared. Thin wafers made by sectioning and polishing samples have high coercive field (higher than 200 Oe) good hysteresis loop squareness (Br/Bm = 0.85), and high figure of merit (2g/a ~ 2). These properties make them well suited for optical mass memory application. This was confirmed experimentally, and a bit density of 5 X 105bit/cm2 was obtained by laser beam thermomagnetic writing. © 1969 IEEE. All rights reserved.