TENSILE, FRACTURE-TOUGHNESS AND FATIGUE CRACK-GROWTH RATE PROPERTIES OF SILICON-CARBIDE WHISKER AND PARTICULATE REINFORCED ALUMINUM METAL MATRIX COMPOSITES

被引：153

作者：

LOGSDON, WA

LIAW, PK

机构：

[1] Westinghouse R&D Cent,, Pittsburgh, PA, USA, Westinghouse R&D Cent, Pittsburgh, PA, USA

来源：

ENGINEERING FRACTURE MECHANICS | 1986年 / 24卷 / 05期

关键词：

Acknowledgements-The authors would like to gratefully acknowledge E. J. Helm; M. G. Peck and R. R. Hovan; Mechanical Behavior Laboratory; for very capably conducting the experiments. The authors are particularly indebted to G. A. Dixon; Exxon Enterprises (Arco/Silag); T; Lynch; DWA Composite Specialties and R. Crowe; Naval Surface Weapons Center; for supplying the silicon carbide whisker and particulate reinforced aluminum metal matrix composites. This work was sponsored by the U’estinghouse Marine Division;

D O I：

10.1016/0013-7944(86)90246-8

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

引用

页码：737 / 751

页数：15

共 45 条

[31]

RACK HJ, 1982, COMMUNICATION DEC

[32]

Ritchie R. O., 1979, International Metals Reviews, V24, P205

[33]

RUSCHAN JJ, 1978, AFMLTR78155 AIR FORC

[34] REVIEW AND EXTENSION OF COMPLIANCE INFORMATION FOR COMMON CRACK GROWTH SPECIMENS [J].

SAXENA, A ;

HUDAK, SJ .

INTERNATIONAL JOURNAL OF FRACTURE, 1978, 14 (05) :453-468

[35]

SAXENA A, 1978, J TESTING EVALUATION, V167

[36]

SCHMIDT RA, 1973, ASTM STP, V536, P79

[37]

STEIN BA, 1983, 5TH P MET MATR COMP

[38] THE INFLUENCE OF ENVIRONMENT AND STRESS RATIO ON FATIGUE CRACK-GROWTH AT NEAR THRESHOLD STRESS INTENSITIES IN LOW-ALLOY STEELS [J].

STEWART, AT .

ENGINEERING FRACTURE MECHANICS, 1980, 13 (03) :463-+

[39] OXIDE-INDUCED CRACK CLOSURE - AN EXPLANATION FOR NEAR-THRESHOLD CORROSION FATIGUE CRACK GROWTH-BEHAVIOR [J].

SURESH, S ;

ZAMISKI, GF ;

RITCHIE, RO .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (08) :1435-1443

[40]

VASUDEVAN AK, COMMUNICATION

← 1 2 3 4 5 →