BehaviorofMgO·Al2O3BasedInclusionsinAlloySteelDuringRefiningProcess

被引：6

作者：

Kent Peaslee

机构：

[1] DepartmentofMaterialsScienceandEngineering,MissouriUniversityofScienceandTechnology

来源：

JournalofIronandSteelResearch(International) | 2010年 / 17卷 / 07期

关键词：

alloy steel; non-metallic inclusion; MgO·Al2O3; spinel; thermodynamics;

D O I：

10.13228/j.boyuan.issn1006-706x.2010.07.004

中图分类号：

TF762.3 [];

学科分类号：

080602 ;

摘要：

The transformation of MgO·Al2O3 based inclusions in alloy steel during refining has been studied by industrial trials.Besides Factsage software is used to study the formation and modification of spinel inclusions in alloy steel using calcium treatment during refining process.The results show that the transformation sequence of inclusions is:MgO·Al2O3→CaO-Al2O3-MgO complex inclusions→MgO·Al2O3,and under present experimental condition,in order to avoid forming MgO·Al2O3 inclusions the content of dissolved Ca in the molten steel has to reach 1×10-6.Also the results show that when more calcium was added to molten steel,the content of Al2O3 and MgO will be lower.Besides,increasing the content of CaO in the inclusions will increase even if the content of SiO2 changes little.

引用

页码：1 / 6

页数：6

共 3 条

[1] 酸蚀法观察钢中夹杂物的三维形貌 [J].

张立峰 ;

李树森 ;

王建伟 ;

佐祥均 .

钢铁, 2009, 44 (03) :75-80

[2]

Formation Mechanism of Spinel-Type Inclusions in High-Alloyed Stainless Steel Melts[J] . Joo Hyun Park.Metallurgical and Materials Transactions B . 2007 (4)

[3] Thermodynamics on the formation of spinel (MgO·Al2O3) inclusion in liquid iron containing chromium [J].

Sung-Koo Jo ;

Seon-Hyo Kim ;

Bo Song .

Metallurgical and Materials Transactions B, 2002, 33 :703-709

← 1 →