磺化间规聚苯乙烯的表征

The effect of different sulfonation degree on properties of sulfonated syndiotactic polystyrene(S s PS) was investigated by 1H NMR, 13 C NMR,FTIR,DSC and WAXD.The results of 13 C NMR showed that a peak at δ =145 5 appeared in all S s PS spectra,which proved that the syndiotactic structure of syndiotactic polystyrene( s PS) still existed in S s PS.With increasing degree of sulfonition,the chemical shifts of C 1 and C\|3 for sulfonated benzene ring turned out to be wider. 1 H NMR spectra showed that C\|3 for sulfonated benzene ring had a chemical shift of 7 66.FTIR spectra showed that sulfonic acid groups were introduced on the para position of benzene rings and with increasing sulfonation degree,the absorption strength of 612/1600 cm 1 ,834/1600cm -1 increased,but the absorption strength of 1078/1600cm -1 decreased.The absorption of ～1030cm -1 ,～1179cm -1 ,～1217cm -1 appeared when the sulfonation degree was higher that 6%. s PS and S s PS H 2 2 had absorption at 975 and 943cm -1 and also had double peaks around ～1175cm -1 ;DSC showed that with increasing sulfonation degree, the glass transition temperature increased, the melt temperature,crystallization temperature and crystallization degree decreased;S s PS couldn't crystallize when sulfonation degree was higher that 6mol%;WAXD proved that s PS had the α and β crystal types, however,S s PS with 2 2% sulfonation degree only had the β crystal type, and S s PS with 6 1% sulfonation degree didn't crystallize.