DMFCs用SPEEK/SiOx-S复合质子交换膜（英文）

A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica powder with sulfonic acid groups(SiOx-S) was added into the SPEEK matrix(DS = 55.1%) to prepare SPEEK/SiOx-S composite membranes.The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder.Pure SPEEK membrane swelled 52.6% at 80°C,whereas the SPEEK/SiOx-S(15%,by mass) membrane swelled only 27.3% at the same temperature.From room temperature to 80℃,all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about o ne order of magnitude lower than that of Nafion?115.Compared with pure SPEEK membranes,the addition of the SiOx-S powder not only leads to higher proton conductivity,but also increases the dimensional stability at higher temperatures,and greater proton conductivity can be achieved at higher temperature.The SPEEK/SiOx-S(20%,by mass) membrane could withstand temperature up to 145°C,at which in 100% relative humidity(RH) its proton conductivity exceeded slightly that of Nafion?115 membrane and reached 0.17 S·cm-1,while pure SPEEK membrane dissolved at 90°C.The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability,high proton conductivity,and low methanol permeability.