聚苯乙烯/蒙脱土纳米复合材料的自组装行为
被引:9
作者:
陈光明
马永梅
漆宗能
机构:
[1] 中国科学院化学研究所分子科学中心工程塑料国家重点实验室!北京
来源:
关键词:
纳米复合材料;
聚苯乙烯;
蒙脱土;
自组装;
D O I:
暂无
中图分类号:
O631 [高分子物理和高分子物理化学];
学科分类号:
摘要:
A shear induced ordered structure in an exfoliated polystyrene(PS)/clay nanocomposite is reported. Self\|assembly behavior was reported for the first time of a shear induced ordered structure in the nanocomposite. The self assembly behavior was measured by X ray diffraction(XRD) patterns, transmission electron microscopy(TEM), and FTIR dichroism technique. Compared with the broad amorphous peaks of the PS, a series of sharp XRD peaks were observed for the exturded PS/clay nanocomposite pellet sample, showing that an ordered sructure occurred under shear flow. The intensities of the four sharp XRD peaks of the ordered sructure decreased significantly with temperature. However, at 95 ℃, the XRD peaks increased significantly, the FTIR dichroism showing that and the phenyl ring of PS changed its orientation from parallel to perpendicular to the monmorillonite primary particles, whereas no obvious orientation of the alkyl chain of PS could be found. At 110 ℃, a disordered structure occurred for the phenyl ring. TEM images confirmed directly that the origin of the ordered structure was mainly due to the planar orientation of the primary particles of silicate layers as well as local ordered microsructure of the primary particles, induced by shear flow. Basd on these investigations, a possible mechanism was deduced for the formation of the ordered strucure induced by shear flow in the exfoliated PS/clay nanocomposite.
引用
收藏
页码:872 / 874
页数:3
相关论文