Slow crack propagation in polyethylene under fatigue at controlled stress intensity

被引:49
作者
Favier, V
Giroud, T
Strijko, E
Hiver, JM
G'Sell, C
Hellinckx, S
Goldberg, A
机构
[1] Ecole Mines, UMR CNRS 7556, Lab Phys Mat, F-54042 Nancy, France
[2] Solvay, Res & Technol Ctr, B-1120 Brussels, Belgium
[3] Solvay Polyolefins Europe, B-1120 Brussels, Belgium
关键词
polyethylene; fatigue; video control;
D O I
10.1016/S0032-3861(01)00701-7
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Fatigue tests were per-formed on circumferentially notched bars (CNB) of high density polyethylene in order to analyse the kinetics and mechanisms of crack propagation. Tests were performed at 80 degreesC in order to accelerate the processes. Unlike standard fatigue procedure in which the force amplitude is constant, the original system utilised in this work was capable of imposing a constant stress intensity amplitude, K-max, during the whole propagation range. This was made possible through the real-time monitoring of crack propagation, a(N), by means of a vi deo-con trolled technique. The results of the tests, for K-max in a range from 0.2 to 0.45 NIPa ml, show that stress intensity is the proper variable which controls crack propagation rate since, on the overall, crack speed is constant at constant K-max and no self-acceleration is observed unlike under force control. The empirical Paris law is verified under all conditions, with a stress intensity exponent close to 4. However, it is shown that constant crack speed is obtained only for K-max < 0.25 MPa m(1/2), when propagation proceeds through the continuous stretching and breaking of microfibrils in the localised craze at the tip of the crack. By contrast, at larger K-max, it is observed that crack tip successively jumps across the extended crazed zone in which very coarse fibrils were previously stretched from voids nucleated in the plane of maximum normal stress at a long distance ahead of the crack tip. (C) 2001 Published by Elsevier Science Ltd.
引用
收藏
页码:1375 / 1382
页数:8
相关论文
共 33 条
[1]  
AHLSTRAND LE, 1998, PLASTICS PIPES, V10, P9
[2]  
BOCKER H, 1992, KUNSTST-GER PLAST+, V82, P739
[3]  
BOYTARD K, 1995, 2 INT C PIP TECHN OS
[4]  
BOYTARD K, 1993, 13 INT PLAST FUEL GA, P291
[5]   SLOW CRACK-GROWTH IN POLYETHYLENE - A REVIEW [J].
BROWN, N ;
LU, XC ;
HUANG, YL ;
QIAN, RZ .
MAKROMOLEKULARE CHEMIE-MACROMOLECULAR SYMPOSIA, 1991, 41 :55-67
[6]   THE FRACTURE-MECHANICS OF SLOW CRACK-GROWTH IN POLYETHYLENE [J].
BROWN, N ;
LU, X .
INTERNATIONAL JOURNAL OF FRACTURE, 1995, 69 (04) :371-377
[7]   THE INITIATION OF SLOW CRACK-GROWTH IN LINEAR POLYETHYLENE UNDER SINGLE EDGE NOTCH TENSION AND PLANE-STRAIN [J].
BROWN, N ;
BHATTACHARYA, SK .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (12) :4553-4560
[8]   A FUNDAMENTAL THEORY FOR SLOW CRACK-GROWTH IN POLYETHYLENE [J].
BROWN, N ;
LU, X .
POLYMER, 1995, 36 (03) :543-548
[9]  
Bucknall C. B., 1985, Plastics and Rubber Processing and Applications, V5, P343
[10]   SLOW STABLE CRACK-GROWTH IN HIGH-DENSITY POLYETHYLENES [J].
CHAN, MKV ;
WILLIAMS, JG .
POLYMER, 1983, 24 (02) :234-244