Ion implantation as a tool to study the oxidation behaviour of TiAl-based intermetallics

被引:25
作者
Stroosnijder, MF [1 ]
Schmutzler, HJ [1 ]
Haanappel, VAC [1 ]
Sunderkotter, JD [1 ]
机构
[1] COMMISS EUROPEAN COMMUNITIES, JOINT RES CTR, INST ADV MAT, I-21020 ISPRA, ITALY
来源
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 1997年 / 48卷 / 01期
关键词
D O I
10.1002/maco.19970480108
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
TiAl-based intermetallic alloys are being considered as structural materials for high-temperature applications due to their low density and substantial mechanical strength at high temperatures. The effect of various elements added by ion implantation on the oxidation behaviour of near-gamma Ti-48Al-2Cr and Ti-48Al-2Cr-2Nb (compositions are given in at-%) in air at 800 degrees C has been studied. Ions implanted (10(17) ions/cm(2)) were Al, Ti, Cr, Mo, Y, Mn, Pt, Nb, and Si in case of Ti-48Al-2Cr and Nb in case of Ti-48Al-2Cr-2Nb. Comparison was made with the oxidation behaviour of Ti-48Al-2Cr-2Nb and Ti-47Al-2Cr-0.2Si alloys in which quaternary elements were added by alloying. It is concluded that ion implantation can serve as a research tool to study, in the frame of screening tests, the influence of various elements on the corrosion behaviour of materials.
引用
收藏
页码:40 / 47
页数:8
相关论文
共 21 条
[1]  
AUSTIN CM, 1993, STRUCTURAL INTERMETALLICS, P143
[2]   OXIDATION BEHAVIOR OF NIAL .2. CAVITY FORMATION BENEATH THE OXIDE SCALE ON NIAL OF DIFFERENT STOICHIOMETRIES [J].
BRUMM, MW ;
GRABKE, HJ .
CORROSION SCIENCE, 1993, 34 (04) :547-&
[3]   THE OXIDATION BEHAVIOR OF NIAL .1. PHASE-TRANSFORMATIONS IN THE ALUMINA SCALE DURING OXIDATION OF NIAL AND NIAL-CR ALLOYS [J].
BRUMM, MW ;
GRABKE, HJ .
CORROSION SCIENCE, 1992, 33 (11) :1677-&
[4]  
CLEMENS H, 1993, STRUCTURAL INTERMETALLICS, P205
[5]   CHARACTERIZATION OF TI-48AL-2CR SHEET MATERIAL [J].
CLEMENS, H ;
RUMBERG, I ;
SCHRETTER, P ;
SCHWANTES, S .
INTERMETALLICS, 1994, 2 (03) :179-184
[6]  
CLEMENS H, 1996, PRAKT METALLOGR, V33, P1
[7]  
Dariola R., 1993, STRUCTURAL INTERMETA
[8]  
HORTON JA, 1995, MRS S P, V364
[9]  
HUANG SC, 1993, STRUCTURAL INTERMETALLICS, P299
[10]  
*IMPL SCI CORP, 1991, PROFILE VERS 3 18