Colloidal nanocrystals of zeolite β stabilized in alumina matrix

被引:56
作者
Landau, MV [1 ]
Tavor, D
Regev, O
Kaliya, ML
Herskowitz, M
Valtchev, V
Mintova, S
机构
[1] Blechner Ctr Ind Catalysis & Proc Dev, Beer Sheva, Israel
[2] Ben Gurion Univ Negev, Dept Chem Engn, IL-84105 Beer Sheva, Israel
[3] Bulgarian Acad Sci, Cent Lab Mineral & Crystallog, Sofia, Bulgaria
关键词
D O I
10.1021/cm980765u
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Characteristics of zeolite beta in stable aqueous colloidal solution were measured by cryo- TEM, DLS, SAXS and after separation from solution by SEM, HR-TEM. Twenty-nanometer spherical zeolite crystals were measured in equilibrium with flocculates. Mixing of colloidal zeolite solution with aluminogel yielded coagulation of both materials. The mass of zeolite: adsorbed by aluminogel increased with decreasing pH. After calcination, pellets of the composite material at zeolite loading below 60 wt % contained separated nanocrystals of 10-15-nm zeolite beta stabilized in the mesopores of alumina matrix. The imbedded zeolite had high structure order and acidity. No blocking of the zeolite micropores in composite materials was detected. The activity of zeolite beta nanocrystals (imbedded in alumina matrix) in cumene cracking twice that of bulk nanozeolite clusters.
引用
收藏
页码:2030 / 2037
页数:8
相关论文
共 17 条
  • [1] PREPARATION OF CATALYSTS BY METALLIC COMPLEX ADSORPTION ON MINERAL OXIDES
    BRUNELLE, JP
    [J]. PURE AND APPLIED CHEMISTRY, 1978, 50 (9-10) : 1211 - 1229
  • [2] Characterization of nanocrystalline zeolite Beta
    Camblor, MA
    Corma, A
    Valencia, S
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 1998, 25 (1-3) : 59 - 74
  • [3] Camblor MA, 1997, STUD SURF SCI CATAL, V105, P341
  • [4] CORRELATIONS BETWEEN LATTICE STRUCTURES OF ZEOLITES AND THEIR SI-29 MAS NMR-SPECTRA - ZEOLITES KZ-2, ZSM-12, AND BETA
    FYFE, CA
    STROBL, H
    KOKOTAILO, GT
    PASZTOR, CT
    BARLOW, GE
    BRADLEY, S
    [J]. ZEOLITES, 1988, 8 (02): : 132 - 136
  • [5] Guinier G Fournet A., 1955, SMALL ANGLE SCATTERI
  • [6] DIFFUSION AND CRYO-TRANSMISSION ELECTRON-MICROSCOPY STUDIES OF BICONTINUOUS MICELLAR SOLUTIONS
    HARWIGSSON, I
    SODERMAN, O
    REGEV, O
    [J]. LANGMUIR, 1994, 10 (12) : 4731 - 4734
  • [7] Landau MV, 1995, STUD SURF SCI CATAL, V94, P357
  • [8] SILICA-SUPPORTED SMALL CRYSTALS OF ZSM-5 ZEOLITE
    LANDAU, MV
    ZAHARUR, N
    HERSKOWITZ, M
    [J]. APPLIED CATALYSIS A-GENERAL, 1994, 115 (01) : L7 - L14
  • [9] Direct force measurements between silica and alumina
    Larson, I
    Drummond, CJ
    Chan, DYC
    Grieser, F
    [J]. LANGMUIR, 1997, 13 (07) : 2109 - 2112
  • [10] LOVALLO MC, 1996, MODERN SYNTHETIC MET, P307