Rheology, morphology and mechanical properties of polyethylene/ethylene vinyl acetate copolymer (PE/EVA) blends

Rheology, morphology and mechanical properties of binary PE and EVA blends together with their thermal behavior were studied. The results of theological studies showed that, for given PE and EVA, the interfacial interaction in PE-rich blends is higher than EVA-rich blends, which in turn led to finer and well-distributed morphology in PE-rich blends, Using two different models, the phase inversion composition was predicted to be in 45 and 47 wt% of the PE phase. This was justified by morphological studies, where a clear co-continuous morphology for 50150 blend was observed. The tensile strength for PE-rich blends showed positive deviation from mixing rule, whereas the 50/50 blend and EVA-rich blends displayed negative deviation. These results were in a good agreement with the results of viscoelastic behavior of the blends. The elongation at break was found to follow the same trend as tensile strength except for 90/10 PE/EVA blend. The latter was explained in terms of the effect of higher co-crystallization in 90/10 composition, which increased the tensile strength and decreased the elongation at break in this composition. The results of thermal behavior of the blends indicated that the melting temperatures of PE and EVA decrease and increase, respectively, due to the dilution effect of EVA on PE and nucleation effect of PE on EVA. (C) 2008 Elsevier Ltd. All rights reserved.