Formation of pores in melt-processed RE-Ba-Cu-O and the techniques to reduce pore density

被引：18

作者：

Sakai, N ^{[1
]}

Ishihara, D ^{[1
]}

Inoue, K ^{[1
]}

Murakami, M ^{[1
]}

机构：

[1] ISTEC, SRL, Minato Ku, Tokyo 1050023, Japan

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2002年 / 15卷 / 05期

关键词：

D O I：

10.1088/0953-2048/15/5/312

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

We have studied the formation of pores in melt-processed RE-Ba-Cu-O. The pores were partly formed due to the oxygen bubbles generated during the peritectic decomposition of RE123 via RE123 --> RE211 + liquid + O-2. When the sample was heated to the temperature high above the peritectic decomposition temperature, a large amount of oxygen gas was generated from the sample. The inert gas entrapment during melting also caused pore formation. The control of the composition, atmosphere and heating conditions was effective in reducing the amount of pores.

引用

收藏

页码：698 / 701

页数：4

相关论文

共 9 条

[1]

IKUTA H, 1999, ADV SUPERCONDUCTIVIT, V11, P657

[2] ROLE OF SILVER ADDITION ON MECHANICAL AND SUPERCONDUCTING PROPERTIES OF HIGH-T-C SUPERCONDUCTORS [J].

JOO, J ;

SINGH, JP ;

WARZYNSKI, T ;

GROW, A ;

POEPPEL, RB .

APPLIED SUPERCONDUCTIVITY, 1994, 2 (06) :401-410

[3] Melt-processed light rare earth element-Ba-Cu-O [J].

Murakami, M ;

Sakai, N ;

Higuchi, T ;

Yoo, SI .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1996, 9 (12) :1015-1032

[4] Sm2BaCuO5 refinement via an attrition milling and CeO2 addition in Sm-Ba-Cu-O systems melt-textured at oxygen partial pressures of 0.001-1 atm [J].

Park, HW ;

Kim, KB ;

Lee, KW ;

Kuk, IH ;

Hong, GW ;

Kim, CJ .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1996, 9 (08) :694-705

[5] DAMAGE CAUSED BY MAGNETIC PRESSURE AT HIGH TRAPPED FIELD IN QUASI-PERMANENT MAGNETS COMPOSED OF MELT-TEXTURED Y-BA-CU-O SUPERCONDUCTOR [J].

REN, Y ;

WEINSTEIN, R ;

LIU, J ;

SAWH, RP ;

FOSTER, C .

PHYSICA C, 1995, 251 (1-2) :15-26

[6] Mechanical properties of Sm-Ba-Cu-O/Ag bulk superconductors [J].

Sakai, N ;

Mase, A ;

Ikuta, H ;

Seo, SJ ;

Mizutani, U ;

Murakami, M .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2000, 13 (06) :770-773

[7] Fabrication of melt-processed RE-Ba-Cu-O bulk superconductors with high densities [J].

Sakai, N ;

Ogasawara, K ;

Inoue, K ;

Ishihara, D ;

Murakami, M .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) :3509-3512

[8] EFFECT OF SILVER AND SILVER-OXIDE ADDITIONS ON THE MECHANICAL AND SUPERCONDUCTING PROPERTIES OF YBA2CU3O7-DELTA SUPERCONDUCTORS [J].

SINGH, JP ;

LEU, HJ ;

POEPPEL, RB ;

VANVOORHEES, E ;

GOUDEY, GT ;

WINSLEY, K ;

SHI, D .

JOURNAL OF APPLIED PHYSICS, 1989, 66 (07) :3154-3159

[9] Mechanical characterization of top-seeded melt-textured YBa2Cu3O7-delta single crystal [J].

Yu, F ;

White, KW ;

Meng, RL .

PHYSICA C, 1997, 276 (3-4) :295-308