Synthesis and characterization of TiB2-reinforced iron-based composites

被引：87

作者：

Anal, A ^{[1
]}

Bandyopadhyay, TK ^{[1
]}

Das, K ^{[1
]}

机构：

[1] Indian Inst Technol, Dept Met & Mat Engn, Kharagpur 721302, W Bengal, India

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2006年 / 172卷 / 01期

关键词：

iron matrix composite; TiB2; aluminothermic reduction; microstructure; hardness; wear resistance;

D O I：

10.1016/j.jmatprotec.2005.09.011

中图分类号：

T [工业技术];

学科分类号：

08 [工学];

摘要：

The TiB2-reinforced iron matrix composite (Fe-TiB2) was synthesized by a simple, cost-effective process involving aluminothermic reduction of blue dust (mainly Fe2O3), titanium dioxide (TiO2) and boron trioxide (B2O3) powder. Aluminothermic reduction of these oxides, being highly exothermic in nature, essentially leads to a self-propagating high-temperature synthesis (SHS) of TiB2-reinforced Fe-based composite. The composite has been subsequently characterized by scanning electron microscopy (SEM), image analysis, X-ray diffraction (XRD), and hardness measurement. It has been found that along with TiB2, Fe2B also forms during the synthesis of composite. Composite, synthesized by this process, possesses high hardness and high temperature stability. The abrasive wear resistance of the composite has been compared with that of a standard wear resistant material, i.e., high-chromium white cast iron, and found to be better than that of the standard material. (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：70 / 76

页数：7

共 20 条

[1]

SYMPATHETIC NUCLEATION - AN OVERVIEW [J].

AARONSON, HI ;

SPANOS, G ;

MASAMURA, RA ;

VARDIMAN, RG ;

MOON, DW ;

MENON, ESK ;

HALL, MG .

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1995, 32 (03) :107-123

[2]

BANDYOPADHYAY PP, 2001, THESIS INDIAN I TECH

[3]

BOYER HE, 1985, METALS HDB, P420

[4]

The incorporation of self-propagating, high-temperature synthesis-formed Fe-TiB2 into ferrous melts [J].

Degnan, CC ;

Shipway, PH .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (09) :2973-2983

[5]

Elevated temperature sliding wear behaviour of TiC-reinforced steel matrix composites [J].

Degnan, CC ;

Shipway, PH ;

Wood, JV .

WEAR, 2001, 251 :1444-1451

[6]

Gaskell D., 1981, INTRO METALLURGICAL, V2nd, P585

[7]

GELLER Y, 1978, TOOL STEELS, P186

[8]

HOLLECK H, 1987, R HM, P149

[9]

SOLIDIFICATION PROCESSING AND TRIBOLOGICAL BEHAVIOR OF PARTICULATE TIC-FERROUS MATRIX COMPOSITES [J].

KATTAMIS, TZ ;

SUGANUMA, T .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 128 (02) :241-252

[10]

PRINCIPLES OF ABRASIVE WEAR [J].

KHRUSCHOV, MM .

WEAR, 1974, 28 (01) :69-88

← 1 2 →