Sol-gel mullite matrix-SiC and -mullite 2D woven fabric composites with or without zirconia containing interphase: Elaboration and properties

被引:38
作者
Colomban, P
Bruneton, E
Lagrange, JL
Mouchon, E
机构
[1] OFF NATL ETUD & RECH AEROSP,OM,F-92322 CHATILLON,FRANCE
[2] CNRS,CTR ETUD CHIM MET,F-94407 VITRY,FRANCE
关键词
D O I
10.1016/0955-2219(95)00189-1
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The properties of composites made with fabrics of Nicalon(R) NLM202 SiC or Nextel(R) 440 mullite fibers are reported. The method used to make composites is a three stages sol-gel process: (i) in situ gelation of a mixture of alkoxides in a ceramic fiber fabric, (ii) the deposit of a matrix precursor onto the impregnated fabrics and (iii) hot-pressing of the stacked fabrics in a carbon mold. The composites have been studied by SEM and TEM. Three point flexural strength has been measured at room temperature and at 900 degrees C in air. Local Young's modulus, microhardness and interfacial shear stress have been determined at RT. Micro-Raman spectra and X-ray microanalysis have been used to study the fiber-interface reactions. Using a mixture of aluminium-silicon ester and tributylborate as interface precursor, we obtained a carbon film free SiC-mullite sliding interface. The use of a complementary ZrO2-GeO2 gel interface precursor allows us to obtain dense composites at a low temperature exhibiting good mechanical properties (linear behaviour up to similar to 180 MPa, even after annealing in air). The effects of a zirconia interphase on the mechanical properties of mullite-mullite composite are also discussed.
引用
收藏
页码:301 / 314
页数:14
相关论文
共 33 条
[1]   INSITU MEASUREMENT OF THE ELASTIC-MODULI OF GLASS-CERAMIC THICK-FILMS [J].
ASHCROFT, IA ;
LAWRENCE, CW ;
WEIHS, TP ;
DERBY, B .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1992, 75 (05) :1284-1286
[2]  
BENOIT M, 1993, HIGH TEMPERATURE CER, P329
[3]   INTERFACE CHARACTERIZATION AND FRACTURE OF CALCIUM ALUMINOSILICATE GLASS-CERAMIC REINFORCED WITH NICALON FIBERS [J].
BLEAY, SM ;
SCOTT, VD ;
HARRIS, B ;
COOKE, RG ;
HABIB, FA .
JOURNAL OF MATERIALS SCIENCE, 1992, 27 (10) :2811-2822
[4]  
BRENNAN JJ, 1990, FIBER REINFORCED CER, P223
[5]  
BRUNETON E, 1993, J PHYS C SOLID STATE, V7, P1937
[6]  
CHEN M, 1990, I PHYS C SEC, V3, P227
[7]   STRUCTURE OF OXIDE GELS AND GLASSES BY INFRARED AND RAMAN-SCATTERING .2. MULLITES [J].
COLOMBAN, P .
JOURNAL OF MATERIALS SCIENCE, 1989, 24 (08) :3011-3020
[8]   NANOCOMPOSITES IN MULLITE-ZRO2 AND MULLITE-TIO2 SYSTEMS SYNTHESIZED THROUGH ALKOXIDE HYDROLYSIS GEL ROUTES - MICROSTRUCTURE AND FRACTOGRAPHY [J].
COLOMBAN, P ;
MAZEROLLES, L .
JOURNAL OF MATERIALS SCIENCE, 1991, 26 (13) :3503-3510
[9]   SINTERING OF ALUMINA AND MULLITES PREPARED BY SLOW HYDROLYSIS OF ALKOXIDES - THE ROLE OF THE PROTONIC SPECIES AND PORE TOPOLOGY [J].
COLOMBAN, P ;
VENDANGE, V .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1992, 147 :245-250
[10]   PHASE-TRANSITION IN, THERMAL HISTORY AND EXPANSION OF NASICON, SOLID-SOLUTION AND LITHIUM DERIVATIVE CERAMICS AND OF SIC (MULLITE) FIBERS NASICON COMPOSITES [J].
COLOMBAN, P ;
MOUCHON, E .
SOLID STATE IONICS, 1994, 73 (3-4) :209-220