Phase development of Bi-2212 superconductor: A time-resolved neutron powder diffraction investigation

被引:6
作者
Argyriou, DN [1 ]
Garcia, JA [1 ]
Mitchell, JF [1 ]
Jorgensen, JD [1 ]
Hinks, DG [1 ]
机构
[1] ARGONNE NATL LAB,DIV SCI MAT,ARGONNE,IL 60439
关键词
D O I
10.1557/JMR.1996.0032
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Time-resolved in situ neutron powder diffraction and Rietveld refinement have been used to study the synthesis of Bi-2212 from hydroxide precursors in a 2% O-2 atmosphere. Bi-2212 was found to form within the temperature range 770-800 degrees C, Studies at 800 degrees C show that Bi-2212 grows rapidly at the expense of Bi-2201. Upon lowering the temperature to 500 degrees C and changing the atmosphere to Ar, a rapid increase in the lattice parameters was observed. We attribute this change to the loss of oxygen from the Bi-2212 lattice. The final material exhibited a T-c of 94 K.
引用
收藏
页码:277 / 280
页数:4
相关论文
共 13 条
[1]   SYNTHESIS OF HIGH-TC SUPERCONDUCTING BI-PBSR-CA-CU-O CERAMICS PREPARED BY AN ULTRASTRUCTURE PROCESSING VIA THE OXALATE ROUTE [J].
CHEN, FH ;
KOO, HS ;
TSENG, TY .
JOURNAL OF MATERIALS SCIENCE, 1990, 25 (07) :3338-3346
[2]   SAMPLE ENVIRONMENTS AT IPNS - PRESENT AND FUTURE CAPABILITIES [J].
FABER, J .
REVUE DE PHYSIQUE APPLIQUEE, 1984, 19 (09) :643-647
[3]   THE INCOMMENSURATE MODULATION OF THE 2212 BI-SR-CA-CU-O SUPERCONDUCTOR [J].
GAO, Y ;
LEE, P ;
COPPENS, P ;
SUBRAMANIAN, MA ;
SLEIGHT, AW .
SCIENCE, 1988, 241 (4868) :954-956
[4]   THE INCOMMENSURATE MODULATION IN THE BI2SR2-XCAXCUO6 SUPERCONDUCTOR, AND ITS RELATION TO THE MODULATION IN BI2SR2-XCAXCU2O8 [J].
GAO, Y ;
LEE, P ;
YE, J ;
BUSH, P ;
PETRICEK, V ;
COPPENS, P .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1989, 160 (5-6) :431-438
[5]   QUANTITATIVE PHASE-ANALYSIS FROM NEUTRON POWDER DIFFRACTION DATA USING THE RIETVELD METHOD [J].
HILL, RJ ;
HOWARD, CJ .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1987, 20 (06) :467-474
[6]  
JORGENSEN JD, 1989, J APPL CRYSTALLOGR, V22, P312
[7]  
LARSON AC, 1990, LAUR8678 LOS AL NAT
[8]  
LEYVA G, 1991, SOLID STATE COMMUN, V8, P887
[9]   THE OXYGEN-CONTENT OF THE HIGH-TEMPERATURE SUPERCONDUCTING COMPOUND BI2+XSR3-YCAYCU2O8+D AS A FUNCTION OF THE CATION CONCENTRATION [J].
MAJEWSKI, P ;
SU, HL ;
ALDINGER, F .
PHYSICA C, 1994, 229 (1-2) :12-16
[10]  
MITCHELL JF, 1995, PHYSICA C, V246, P126