Fabrication and electrical properties of lead zirconate titanate thick films

被引:129
作者
Chen, HD [1 ]
Udayakumar, KR [1 ]
Gaskey, CJ [1 ]
Cross, LE [1 ]
Bernstein, JJ [1 ]
Niles, LC [1 ]
机构
[1] CHARLES STARK DRAPER LAB INC,CAMBRIDGE,MA 02139
关键词
D O I
10.1111/j.1151-2916.1996.tb08957.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Thick films of lead zirconate titanate of the morphotropic phase boundary composition, Pb(Zr0.52Ti0.48)O-3, have been fabricated on platinum-buffered silicon using a modified sol-gel spin-coating technique, Crack-free films of 12-mu m thickness can be uniformly deposited on 3-in.-diameter wafers with high yield and properties comparable to those of bulk ceramics, The thickness dependence of film structure and the dielectric, ferroelectric, and piezoelectric properties have been characterized over the thickness range of 1-12 mu m. A strong (100) texture develops as film thickness increases above 5 mu m; the films were marked by saturation values of longitudinal piezoelectric coefficient d(33), 340 pC/N; remanent polarization, 27 mu C/cm(2); and dielectric permittivity, 1450, PZT films in this thickness range are extremely well-suited to application as electromechanical transduction media in silicon-based microelectromechanical systems (MEMS).
引用
收藏
页码:2189 / 2192
页数:4
相关论文
共 8 条
[1]  
BARROW DA, 1995, MATER RES SOC SYMP P, V360, P103
[2]   CHEMICAL ASPECTS OF SOLUTION ROUTES TO PEROVSKITE-PHASE MIXED-METAL OXIDES FROM METAL-ORGANIC PRECURSORS [J].
CHANDLER, CD ;
ROGER, C ;
HAMPDENSMITH, MJ .
CHEMICAL REVIEWS, 1993, 93 (03) :1205-1241
[3]   DIELECTRIC BREAKDOWN OF POROUS CERAMICS [J].
GERSON, R ;
MARSHALL, TC .
JOURNAL OF APPLIED PHYSICS, 1959, 30 (11) :1650-1653
[4]  
Jaffe H., 1971, PIEZOELECTRIC CERAMI, P146
[5]   THICKNESS-DEPENDENT ELECTRICAL CHARACTERISTICS OF LEAD-ZIRCONATE-TITANATE FILMS [J].
UDAYAKUMAR, KR ;
SCHUELE, PJ ;
CHEN, J ;
KRUPANIDHI, SB ;
CROSS, LE .
JOURNAL OF APPLIED PHYSICS, 1995, 77 (08) :3981-3986
[6]  
WILSON OB, 1988, INTRO THEORY DESIGN, P155
[7]  
YI G, 1992, P 8 IEEE INT S APPL, P289
[8]   PREPARATION OF PB(ZR,TI)O3 THIN-FILMS BY SOL-GEL PROCESSING - ELECTRICAL, OPTICAL, AND ELECTRO-OPTIC PROPERTIES [J].
YI, GH ;
WU, Z ;
SAYER, M .
JOURNAL OF APPLIED PHYSICS, 1988, 64 (05) :2717-2724