Hot deformation mechanisms in ELI grade Ti-6Al-4V

被引:129
作者
Seshacharyulu, T [1 ]
Medeiros, SC [1 ]
Morgan, JT [1 ]
Malas, JC [1 ]
Frazier, WG [1 ]
Prasad, YVRK [1 ]
机构
[1] USAF, Res Lab, Mat & Mfg Directorate, Mat Proc Design Branch, Wright Patterson AFB, OH 45433 USA
关键词
Ti-6Al-4V; hot working; microstructure; mechanisms;
D O I
10.1016/S1359-6462(99)00163-3
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The processing map developed on Ti-6-4 with Widmanstatten starting microstructure revealed the material exhibits globularization in the α-β phase field while the β phase deforms by the mechanism of large-grained superplasticity. The apparent activation energy of hot deformation in the α-β range using kinetic analysis yielded a value of 453 kJ/mole, while a value of 165-240 kJ/mole is obtained using Schock and Kocks models. The latter value of activation energy together with an estimated activation volume of 13-85 b3 suggests that cross-slip is the rate controlling mechanism for globularization. The apparent activation energy for β large-grained superplasticity matches well with that of self-diffusion in β.
引用
收藏
页码:283 / 288
页数:6
相关论文
共 9 条
[1]   DEFORMATION MECHANISMS IN COMMERCIAL TI-50A (0.5 AT PCT OEQ) AT INTERMEDIATE AND HIGH-TEMPERATURES (0.3 - 0.6TM) [J].
DONER, M ;
CONRAD, H .
METALLURGICAL TRANSACTIONS, 1973, 4 (12) :2809-2817
[2]   Self-Diffusion of Ti, Zr, and Hf in their HCP Phases, and Diffusion of Nb-95 in HCP Zr [J].
Dyment, F. ;
Libanati, C. M. .
JOURNAL OF MATERIALS SCIENCE, 1968, 3 (04) :349-359
[3]  
Frost H.J., 1982, Deformation Mechanism Maps, P44
[4]  
KOCKS UF, 1975, PROGR MATERIALS SCI, V19, P110
[5]  
MANONEY MW, 1994, MAT PROPERTIES HDB T, P1101
[6]  
Nieh T.G., 1997, Superplasticity in Metals and Ceramics, DOI 10.1017/CBO9780511525230
[7]  
Prasad Y.V. R. K., 1997, Hot Working Guide: A Compendium of Processing Maps, V1st Editio
[8]  
PRASAD YVRK, 1990, INDIAN J TECHNOL, V28, P435
[9]  
Schock G., 1980, Dislocations in solids, vol.3. Moving dislocations, P63