A study on corrosion resistance characteristics of PVD Cr-N coated steels by electrochemical method

The corrosion behavior of Cr-N coated steels with different phases (alpha-Cr, CrN and Cr2N) deposited by cathodic arc deposition on AISI H13 steel was investigated in a 3.5% NaCl solution at ambient temperature. Potentiodynamic polarization tests, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) were the techniques applied to characterize the corrosion behavior. It was found that the CrN coating had a lower current density from potentiodynamic polarization tests than others. The porosity, corresponding to the ratio of the polarization resistance of the uncoated and the coated substrate, was higher in the Cr2N coating than in the other Cr-N coated steels. EIS measurements showed, for most of the Cr-N coated steels, that the Bode plot presented two time constants. Also, the Cr2N coating represented the characteristic of Warburg behavior after 72 It of immersion. The coating morphologies were examined in planar view and cross-section by SEM analysis and the results were compared with those of the electrochemical measurements The CrN coating had a dense, columnar grain-sized microstructure with minor intergranular porosity. From the above results, it is concluded that the CrN coating provided a better corrosion protection than the other Cr-N coated steels. (C) 2002 Elsevier Science B.V. All rights reserved.