Electrochemical copolymerization of aniline and metanilic acid

被引:91
作者
Lee, JY
Cui, CQ
机构
[1] Department of Chemical Engineering, National University of Singapore, Singapore 0511
关键词
electrodeposition; copolymerization; aniline; metanilic acid;
D O I
10.1016/0022-0728(95)04215-6
中图分类号
O65 [分析化学];
学科分类号
070302 ; 081704 ;
摘要
Copolymers of metanilic acid (MA) and aniline (An) were electrodeposited by cyclic voltammetry from dilute H2SO4 containing 0.1 M of MA and varying amounts of An. The MA content in the copolymers was determined by Fourier transform IR (FTIR) and UV-visible analyses of spectral features attributable to MA. It is found that the MA content decreases with film thickness, and with increasing acidity and An concentration in the depositing solutions. The results are interpreted in terms of the limited involvement of MA monomers in copolymerization, particularly in the late stage of polymer growth. The presence of MA units in copolymers are not detectable at An/MA ratios approaching unity. Although MA monomers are incorporated only sporadically, extended polymer growth is inhibited even by trace quantities of MA because of the unfavourable combination of inductive and steric effects imposed by the bulky sulphonate pendant groups.
引用
收藏
页码:109 / 116
页数:8
相关论文
共 24 条
[1]   SPECTROSCOPIC AND ELECTRICAL CHARACTERIZATION OF SOME ANILINE OLIGOMERS AND POLYANILINE [J].
CAO, Y ;
LI, SZ ;
XUE, ZJ ;
GUO, D .
SYNTHETIC METALS, 1986, 16 (03) :305-315
[2]   POLYANILINE - PROTONIC ACID DOPING OF THE EMERALDINE FORM TO THE METALLIC REGIME [J].
CHIANG, JC ;
MACDIARMID, AG .
SYNTHETIC METALS, 1986, 13 (1-3) :193-205
[3]   MEASUREMENT OF THE EXTENT OF IMPURITY INCORPORATION DURING POTENTIOSTATIC AND CYCLIC POTENTIAL SWEEP DEPOSITIONS OF POLYANILINE [J].
CUI, CQ ;
ONG, LH ;
TAN, TC ;
LEE, JY .
SYNTHETIC METALS, 1993, 58 (02) :147-160
[4]   EXTENT OF INCORPORATION OF HYDROLYSIS PRODUCTS IN POLYANILINE FILMS DEPOSITED BY CYCLIC POTENTIAL SWEEP [J].
CUI, CQ ;
ONG, LH ;
TAN, TC ;
LEE, JY .
ELECTROCHIMICA ACTA, 1993, 38 (10) :1395-1404
[5]   DEGRADATION OF COPOLYMERS OF ANILINE AND METANILIC ACID [J].
CUI, CQ ;
SU, XH ;
LEE, JY .
POLYMER DEGRADATION AND STABILITY, 1994, 43 (02) :245-252
[6]   MEASUREMENT AND EVALUATION OF POLYANILINE DEGRADATION [J].
CUI, CQ ;
SU, XH ;
LEE, JY .
POLYMER DEGRADATION AND STABILITY, 1993, 41 (01) :69-76
[7]   CYCLIC VOLTAMMETRY OF POLYANILINE - INTERPRETATION OF THE MIDDLE PEAK [J].
GENIES, EM ;
LAPKOWSKI, M ;
PENNEAU, JF .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1988, 249 (1-2) :97-107
[8]   SPECTROELECTROCHEMICAL STUDY OF POLYPYRROLE FILMS [J].
GENIES, EM ;
BIDAN, G ;
DIAZ, AF .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1983, 149 (1-2) :101-113
[9]   ANODIC-OXIDATION PATHWAYS OF N-ALKYLANILINES [J].
HAND, RL ;
NELSON, RF .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1974, 96 (03) :850-860
[10]   MODIFIED POLYANILINE THROUGH SIMULTANEOUS ELECTROCHEMICAL POLYMERIZATION OF ANILINE AND METANILIC ACID [J].
LEE, JY ;
CUI, CQ ;
SU, XH ;
ZHOU, MS .
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1993, 360 (1-2) :177-187