A facile one-pot synthesis of mesoporous graphite-like carbon through the organic-organic co-assembly

被引:23
作者
Wang, Anmiao [1 ]
Ren, Jiawen [1 ]
Shi, Bianfang [1 ]
Lu, Guanzhong [1 ]
Wang, Yanqin [1 ]
机构
[1] E China Univ Sci & Technol, Key Lab Adv Mat, Res Inst Ind Catalysis, Shanghai 200237, Peoples R China
基金
中国国家自然科学基金;
关键词
Mesoporous carbon; Graphitization; Ammonium ferric citrate; Catalytic properties; ORDERED POROUS CARBON; HIGH-SURFACE-AREA; CATALYTIC GRAPHITIZATION; NANOPOROUS CARBON; MOLECULAR-SIEVES; POLYMERS; NANOPARTICLES; ROUTE; TRANSFORMATION; NANOCOMPOSITE;
D O I
10.1016/j.micromeso.2011.10.022
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Mesoporous carbon materials with partially graphitized structure were synthesized by a one-pot, co-assembly of tri-block copolymer with phenolic resin under the assistance of ammonium ferric citrate. The structure was characterized by XRD, TEM, N-2 sorption and TG/DTA. The mesoporous structure of the polymer conserved after the addition of ammonium ferric citrate. The graphitization of carbon material was achieved at lower temperature (700 degrees C), which was attributed to the catalytic property of iron, as well as the formation of carbon-polymer structure pre-carbonized at 350 degrees C. The final graphitic porous carbon materials had high surface area and performed well in the selective oxidation of benzyl alcohol to benzaldehyde. The selectivity to benzaldehyde reached 96.2%. Crown Copyright (C) 2011 Published by Elsevier Inc. All rights reserved.
引用
收藏
页码:287 / 292
页数:6
相关论文
共 35 条
[1]   Synthesis and structural characteristics of carbon aerogels with a high content of Fe, Co, Ni, Cu, and Pd [J].
Cotet, L. C. ;
Gich, M. ;
Roig, A. ;
Popescu, I. C. ;
Cosoveanu, V. ;
Molins, E. ;
Danciu, V. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2006, 352 (26-27) :2772-2777
[2]   Characterization of activated carbon, graphitized carbon fibers and synthetic diamond powder using TPD and drifts [J].
Dandekar, A ;
Baker, RTK ;
Vannice, MA .
CARBON, 1998, 36 (12) :1821-1831
[3]   Ultra-Large-Pore Mesoporous Carbons Templated from Poly(ethylene oxide)-b-Polystyrene Diblock Copolymer by Adding Polystyrene Homopolymer as a Pore Expander [J].
Deng, Yonghui ;
Liu, Jia ;
Liu, Chong ;
Gu, Dong ;
Sun, Zhenkun ;
Wei, Jing ;
Zhang, Junyong ;
Zhang, Lijuan ;
Tu, Bo ;
Zhao, Dongyuan .
CHEMISTRY OF MATERIALS, 2008, 20 (23) :7281-7286
[4]   Synthesis of Partially Graphitic Ordered Mesoporous Carbons with High Surface Areas [J].
Gao, Wenjun ;
Wan, Ying ;
Dou, Yuqian ;
Zhao, Dongyuan .
ADVANCED ENERGY MATERIALS, 2011, 1 (01) :115-123
[5]   Growth of Single-Crystal Mesoporous Carbons with Im(3)over-barm Symmetry [J].
Gu, Dong ;
Bongard, Hans ;
Meng, Yan ;
Miyasaka, Keiichi ;
Terasaki, Osamu ;
Zhang, Fuqiang ;
Deng, Yonghui ;
Wu, Zhangxiong ;
Feng, Dan ;
Fang, Yin ;
Tu, Bo ;
Schueth, Ferdi ;
Zhao, Dongyuan .
CHEMISTRY OF MATERIALS, 2010, 22 (16) :4828-4833
[6]   Carbon/MoO2 composite based on porous semi-graphitized nanorod assemblies from in situ reaction of tri-block polymers [J].
Ji, Xiulei ;
Herle, Subramanya ;
Rho, Youngho ;
Nazar, L. F. .
CHEMISTRY OF MATERIALS, 2007, 19 (03) :374-383
[7]   Ordered nanoporous arrays of carbon supporting high dispersions of platinum nanoparticles [J].
Joo, SH ;
Choi, SJ ;
Oh, I ;
Kwak, J ;
Liu, Z ;
Terasaki, O ;
Ryoo, R .
NATURE, 2001, 412 (6843) :169-172
[8]   Synthesis of new, nanoporous carbon with hexagonally ordered mesostructure [J].
Jun, S ;
Joo, SH ;
Ryoo, R ;
Kruk, M ;
Jaroniec, M ;
Liu, Z ;
Ohsuna, T ;
Terasaki, O .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2000, 122 (43) :10712-10713
[9]   A synthetic route to ordered mesoporous carbon materials with graphitic pore walls [J].
Kim, TW ;
Park, IS ;
Ryoo, R .
ANGEWANDTE CHEMIE-INTERNATIONAL EDITION, 2003, 42 (36) :4375-4379
[10]   Carbon nanotubes from polyethylene precursors: Structure and structural changes caused by thermal and chemical treatment revealed by HREM [J].
Kiselev, NA ;
Sloan, J ;
Zakharov, DN ;
Kukovitskii, EF ;
Hutchison, JL ;
Hammer, J ;
Kotosonov, AS .
CARBON, 1998, 36 (7-8) :1149-1157