Enhancement of bifunctional catalysis by Ir doping of La0.6Ca0.4CoO3 perovskites

被引：15

作者：

Chang, Yun-Min ^{[1
]}

Hsieh, Yu-Chi ^{[1
]}

Wu, Pu-Wei ^{[1
]}

Lai, Chun-Han ^{[1
]}

Chang, Tin-Yu ^{[1
]}

机构：

[1] Natl Chiao Tung Univ, Dept Mat Sci & Engn, Hsinchu 300, Taiwan

来源：

MATERIALS LETTERS | 2008年 / 62卷 / 26期

关键词：

perovskites; catalysts; bifunctional abilities; alkaline electrolyte;

D O I：

10.1016/j.matlet.2008.06.040

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

La0.6Ca0.4Co0.8Ir0.2O3 was prepared by solid state reaction synthesis from mixtures of La(NO3)(3)center dot 6H(2)O, Ca (NO3)(2)center dot 4H(2)O, Co(NO3)(3)center dot 6H(2)O, and IrO2 at stoichiometric ratio. Images from scanning electron microscopy on the as-synthesized powders exhibited particles in irregular shape at 100-250 nm in size. X-ray diffraction analysis confirmed the formation of perovskite without the rutile signals from IrO2, suggesting successful incorporation of Ir4+ at the Co cation sites. The carbon nanocapsules (CNCs) were used as an electrocatalyst support. Electrodes for electrochemical measurements were fabricated by depositing mixtures of CNCs, La0.6Ca0.4Co0.8Ir0.2O3 and polymeric binders on commercially available noncatalyzed gas diffusion electrodes. In alkaline electrolyte, the La0.6Ca0.4Co0.8Ir0.2O3/CNCs demonstrated superior performances than those of La0.6Ca0.4Co0.8Ir0.2O3/CNCs and IrO2/CNCs in both charging and discharging current-potential polarization measurements. (c) 2008 Elsevier B.V. All rights reserved.

引用

页码：4220 / 4222

页数：3

共 13 条

[1] Mechanical alloying preparation of La0.6Ca0.4CoIr0.25O3.5-δ as a bifunctional electrocatalyst in alkaline electrolyte [J].

Chang, Yun-Min ;

Wu, Pu-Wei ;

Wu, Cheng-Yeou ;

Hsieh, Yi-Fan ;

Chen, Jing-Yu .

ELECTROCHEMICAL AND SOLID STATE LETTERS, 2008, 11 (04) :B47-B50

[2] Composite materials for electrocatalysis of O2 evolution:: IrO2+SnO2 in acid solution [J].

De Pauli, CP ;

Trasatti, S .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2002, 538 :145-151

[3] Bifunctional oxygen/air electrodes [J].

Jörissen, L .

JOURNAL OF POWER SOURCES, 2006, 155 (01) :23-32

[4]

Kinoshita K., 1992, Electrochemical Oxygen Technology

[5] Thermal treatment of La0.6Ca0.4CoO3 perovskites for bifunctional air electrodes [J].

Lee, CK ;

Striebel, KA ;

McLarnon, FR ;

Cairns, EJ .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1997, 144 (11) :3801-3806

[6] Carbon nanocapsules as an electrocatalyst support for the oxygen reduction reaction in alkaline electrolyte [J].

Lin, Y. M. ;

Chang, Y. M. ;

Wu, P. W. ;

Lin, P. ;

Li, Y. Y. ;

Wu, C. Y. ;

Tsai, C. F. ;

Yeh, K. Y. .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 2008, 38 (04) :507-514

[7] Synthesis of carbon nanocapsules and carbon nanotubes by an acetylene flame method [J].

Liu, Ting-Chi ;

Li, Yuan-Yao .

CARBON, 2006, 44 (10) :2045-2050

[8] BI-FUNCTIONAL OXYGEN-ELECTRODE USING LARGE SURFACE-AREA LA1-XCAXCOO3 FOR RECHARGEABLE METAL-AIR BATTERY [J].

SHIMIZU, Y ;

UEMURA, K ;

MATSUDA, H ;

MIURA, N ;

YAMAZOE, N .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1990, 137 (11) :3430-3433

[9] Effects of Ni, Fe, Cu, and Cr substitutions for Co in La0.8Sr0.2CoO3 on electrocatalytic properties for oxygen evolution [J].

Tiwari, SK ;

Singh, SP ;

Singh, RN .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1996, 143 (05) :1505-1510

[10]

Trasatti S., 1994, ELECTROCHEMISTRY NOV, P207

← 1 2 →