Nanoporous anatase ceramic membranes as fast-proton-conducting materials

被引:21
作者
Colomer, MT [1 ]
机构
[1] CSIC, Inst Ceram & Vidrio, E-28049 Madrid, Spain
关键词
nanoporous anatase; electrical conductivity; fuel cells; TiO2; proton conduction;
D O I
10.1016/j.jeurceramsoc.2005.01.035
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Nanoporous anatase ceramic membranes were prepared via particulate sol-gel processes. The calcined xeroggels were mesoporous. with a BET Surface area of 121 m(2)/g, an average pore diameter of 5.8 nm and a pore volume of 0.236 cm(3)/g. Proton conductivity of the membranes was measured as a function of temperature and relative humidity, R.H. When anatase membranes are treated at pH 1.5. the proton conductivity increased in the whole range of temperature and R.H. It indicates that the surface site density (number of water molecules per square nanometer) of these materials has a strong effect oil conductivity. The proton conductivity of the studied anatase membranes followed an Arrhenius-like dependence oil the temperature (from room temperature to 90 degrees C), in both treated and untreated membranes. A sigmoidal dependence of the conductivity Oil the R.H. was observed with the greatest increase noted between 58 and 81% R.H. in both treated and untreated anatase membranes. The highest value of proton conductivity was found to be 0.015 S/cm at 90 degrees C and 81% R.H., for treated anatase ceramic membranes. An increase of the conductivity could be achieved by means of longer times of treatment. According to the activation energy values, proton migration in this kind of materials Could be dominated by the Grotthuss mechanism in the whole range of R.H. The similar values of proton conductivity, lower cost and higher hydrophilicity of these membranes make them potential substitutes for perfluorosulfonic polymeric membranes in proton exchange membrane fuel cells (PEMFCs). (c) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码:1231 / 1236
页数:6
相关论文
共 25 条
[1]   Hydrogen bonds, water rotation and proton mobility [J].
Agmon, N .
JOURNAL DE CHIMIE PHYSIQUE ET DE PHYSICO-CHIMIE BIOLOGIQUE, 1996, 93 (10) :1714-1736
[2]   Impedance spectroscopic studies of sol-gel derived subcritically dried silica aerogels [J].
Anappara, AA ;
Rajeshkumar, S ;
Mukundan, P ;
Warrier, PRS ;
Ghosh, S ;
Warrier, KGK .
ACTA MATERIALIA, 2004, 52 (02) :369-375
[3]   THE DETERMINATION OF PORE VOLUME AND AREA DISTRIBUTIONS IN POROUS SUBSTANCES .1. COMPUTATIONS FROM NITROGEN ISOTHERMS [J].
BARRETT, EP ;
JOYNER, LG ;
HALENDA, PP .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1951, 73 (01) :373-380
[4]  
Boukamp B., 1988, EQUIVALENT CIRCUIT E
[5]  
Colomban P., 1992, PROTON CONDUCTORS SO, P38
[6]   High porosity silica xerogels prepared by a particulate sol-gel route: pore structure and proton conductivity [J].
Colomer, MT ;
Anderson, MA .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2001, 290 (2-3) :93-104
[7]   ISOTHERM EQUATION FOR WATER-VAPOR ADSORPTION BY MICROPOROUS CARBONACEOUS ADSORBENTS [J].
DUBININ, MM ;
SERPINSKY, VV .
CARBON, 1981, 19 (05) :402-403
[8]  
GOTTESFELD S, 1997, POLYM ELECTROLYTE FU, P245
[9]  
GREGG SJ, 1982, ADSORPTION SURFACE
[10]   Nanostructure of Nafion® membranes at different states of hydration -: An IR and Raman study [J].
Gruger, A ;
Régis, A ;
Schmatko, T ;
Colomban, P .
VIBRATIONAL SPECTROSCOPY, 2001, 26 (02) :215-225