The electrochemical corrosion of pure magnesium in 1 N NaCl

被引：596

作者：

Song, G ^{[1
]}

Atrens, A ^{[1
]}

Stjohn, D ^{[1
]}

Nairn, J ^{[1
]}

Li, Y ^{[1
]}

机构：

[1] ACAD SINICA,STATE KEY LAB CORROS & PROTECT,INST CORROS & PROTECT MET,SHENYANG 110015,PEOPLES R CHINA

来源：

CORROSION SCIENCE | 1997年 / 39卷 / 05期

关键词：

magnesium; electrochemical corrosion; cathodic protection; STM;

D O I：

10.1016/S0010-938X(96)00172-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

An electrochemical investigation was carried out to study the corrosion of pure magnesium in 1 N NaCl at different pH values involving electrochemical polarisation, scanning tunnel microscopy (STM), measurement of hydrogen gas evolution and measurement of the elements dissolved from the magnesium specimen which were determined by inductively coupled plasma atomic emission spectrophotometry (ICPAES). A partially protective surface film was a principal factor controlling corrosion. Film coverage decreased with increasing applied electrode potential. Application of a suitable external cathodic current density was shown to inhibit magnesium dissolution whilst at the same time the hydrogen evolution rate was relatively small. This showed that cathodic protection could be used to significantly reduce magnesium corrosion. A new definition is proposed for the negative difference effect (NDE). (C) 1997 Elsevier Science Ltd.

引用

页码：855 / 875

页数：21

共 22 条

[1]

[Anonymous], INT MAT REV

[2]

BROUILLET P, 1954, CR HEBD ACAD SCI, V239, P1795

[3]

BRUN CH, 1976, MEM ETUD SCI REV MET, V73, P659

[4]

BUSK RS, 1986, MAGNESIUM PRODUCTS D

[5] DISSOLUTION AND HYDRATION KINETICS OF MGO [J].

FRUHWIRTH, O ;

HERZOG, GW ;

HOLLERER, I ;

RACHETTI, A .

SURFACE TECHNOLOGY, 1985, 24 (03) :301-317

[6] ANODIC BEHAVIOR OF MG IN HC03-/CO23- BUFFER SOLUTIONS, QUASI-STEADY MEASUREMENTS [J].

GULBRANDSEN, E .

ELECTROCHIMICA ACTA, 1992, 37 (08) :1403-1412

[7] THE PASSIVE BEHAVIOR OF MG IN ALKALINE FLUORIDE SOLUTIONS - ELECTROCHEMICAL AND ELECTRON-MICROSCOPIC INVESTIGATIONS [J].

GULBRANDSEN, E ;

TAFTO, J ;

OLSEN, A .

CORROSION SCIENCE, 1993, 34 (09) :1423-1440

[8]

Hanawalt JD, 1942, T AM I MIN MET ENG, V147, P273

[9]

HULL MN, 1972, J ELECT CHEM, V38

[10]

Maker G. L., 1988, ADV MAGNESIUM ALLOYS, P105

← 1 2 3 →