Synthesis and thermal stability of beta zeolite using ammonium fluoride

被引：48
作者：
Jon, H
Lu, BW [1 ]
Oumi, Y
Itabashi, K
Sano, T
机构：
[1] Japan Adv Inst Sci & Technol, Sch Mat Sci, Nomi, Ishikawa 9231292, Japan
[2] Tosoh Corp, Nanyo Res Lab, Yamaguchi 7468501, Japan
来源：
MICROPOROUS AND MESOPOROUS MATERIALS | 2006年 / 89卷 / 1-3期
关键词：
beta; zeolite; ammonium fluoride; hydrothermal synthesis; thermal stability;
D O I：
10.1016/j.micromeso.2005.10.016
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Hydrothermal synthesis of beta (BEA) zeolite with NH4F as a fluoride source was investigated in detail. The highly crystalline BEA zeolites with a wide range of Si/Al ratios from 10 to infinity could be easily obtained. From an evaluation of the thermal stability of BEA zeolites synthesized with and without NH4F, it was found that the thermal stability of BEA zeolite synthesized with NH4F is relatively higher than that of BEA zeolite synthesized without NH4F, although the thermal stability decreases with an increase in the Al content. The addition of NaOH hardly affected the thermal stability of BEA zeolite synthesized with NH4F. The enhanced thermal stability was attributed to much less framework defects. (c) 2005 Elsevier Inc. All rights reserved.
引用
收藏
页码：88 / 95
页数：8
相关论文
共 18 条
[1]   Synthesis in fluoride media and characterisation of aluminosilicate zeolite beta [J].
Camblor, MA ;
Corma, A ;
Valencia, S .
JOURNAL OF MATERIALS CHEMISTRY, 1998, 8 (09) :2137-2145
[2]   High silica zeolites with three-dimensional systems of large pore channels [J].
Camblor, MA ;
Barrett, PA ;
Díaz-Cabañas, MJ ;
Villaescusa, LA ;
Puche, M ;
Boix, T ;
Pérez, E ;
Koller, H .
MICROPOROUS AND MESOPOROUS MATERIALS, 2001, 48 (1-3) :11-22
[3]  
CHAMBLOR MA, 1996, CHEM COMMUN, P2365
[4]   HIGH-RESOLUTION SOLID-STATE SI-29 AND C-13 NMR ON HIGHLY SILICEOUS MFI-TYPE ZEOLITES SYNTHESIZED IN NONALKALINE FLUORIDE MEDIUM [J].
CHEZEAU, JM ;
DELMOTTE, L ;
GUTH, JL ;
SOULARD, M .
ZEOLITES, 1989, 9 (01) :78-80
[5]   INFLUENCE OF SYNTHESIS CONDITIONS AND POSTSYNTHESIS TREATMENTS ON THE NATURE AND QUANTITY OF STRUCTURAL DEFECTS IN HIGHLY SILICEOUS MFI ZEOLITES - A HIGH-RESOLUTION SOLID-STATE SI-29 NMR-STUDY [J].
CHEZEAU, JM ;
DELMOTTE, L ;
GUTH, JL ;
GABELICA, Z .
ZEOLITES, 1991, 11 (06) :598-606
[6]   THE FRAMEWORK TOPOLOGY OF ZEOLITE-BETA [J].
HIGGINS, JB ;
LAPIERRE, RB ;
SCHLENKER, JL ;
ROHRMAN, AC ;
WOOD, JD ;
KERR, GT ;
ROHRBAUGH, WJ .
ZEOLITES, 1988, 8 (06) :446-452
[7]   Synthesis of zeolite beta in fluoride media under microwave irradiation [J].
Kim, DS ;
Chang, JS ;
Hwang, JS ;
Park, SE ;
Kim, JM .
MICROPOROUS AND MESOPOROUS MATERIALS, 2004, 68 (1-3) :77-82
[8]   Control of the morphology of all-silica BEA-type zeolite synthesized in basic media [J].
Larlus, O ;
Valtchev, VP .
CHEMISTRY OF MATERIALS, 2005, 17 (04) :881-886
[9]   Effect of ammonium salts on hydrothermal synthesis of high-silica mordenite [J].
Lu, BW ;
Oumi, Y ;
Itabashi, K ;
Sano, T .
MICROPOROUS AND MESOPOROUS MATERIALS, 2005, 81 (1-3) :365-374
[10]  
NEWMAN JM, 1988, P ROY SOC LOND A MAT, V420, P375
12