Environmental stability of the YSZ layer and the YSZ/TGO interface of an in-service EB-PVD coated high-pressure turbine blade

被引：40

作者：

Braue, Wolfgang ^{[1
]}

机构：

[1] DLR, German Aerosp Ctr, Mat Res Inst, D-51147 Cologne, Germany

来源：

JOURNAL OF MATERIALS SCIENCE | 2009年 / 44卷 / 07期

关键词：

THERMAL-BARRIER COATINGS; CALCIUM ZIRCONIUM SILICATE; SULFIDATION CORROSION; MECHANISMS; SYSTEM; DEGRADATION; PERFORMANCE; SULFATES; VANADIUM;

D O I：

10.1007/s10853-008-3215-8

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Hot corrosion of an in-service EB-PVD coated 1st stage high-pressure turbine (HPT) blade following an interactive CaSO4 infiltration/CMAS deposition process has produced reactive interfaces with the yttria stabilized zirconia (YSZ) top coat and the TGO layer which were investigated by analytical scanning and transmission electron microscopy (TEM). Despite complete CaSO4 infiltration of the coating macroscopic damage of the airfoil was confined to the pressure surface close to the trailing edge. Since the bulk composition of the CaSO4/CMAS deposits exhibited a high lime-to-silica ratio CaSO4/CMAS/YSZ interfaces typically involved a Ca-Zr-rich layer followed by fine-grained Ca-FSZ particles enveloping rounded YSZ column tips. No interfacial reaction was observed between the YSZ column walls and the CaSO4 pore fillings. Possible terms for the formation of this unique CaSO4/CMAS microstructure are evaluated. Zirconia destabilization upon hot corrosion is discussed in the light of phase compatibilities in the systems CaO-Y2O3-ZrO2 and CaO-ZrO2-SiO2 and put into perspective with previous work on both, natural and synthetic hot corrosion deposits.

引用

页码：1664 / 1675

页数：12

共 51 条

[1] BAGHDADITE, A NEW CALCIUM ZIRCONIUM SILICATE MINERAL FROM IRAQ [J].

ALHERMEZI, HM ;

MCKIE, D ;

HALL, AJ .

MINERALOGICAL MAGAZINE, 1986, 50 (355) :119-123

[2]

[Anonymous], 1998, PHASE DIAGRAMS ZIRCO

[3]

Ansell HG, 1980, CAN MINERAL, V18, P201

[4] Experimental and MD simulations study of CaO-ZrO2-SiO2 glasses [J].

Barbieri, L ;

Cannillo, V ;

Leonelli, C ;

Montorsi, M ;

Mustarelli, P ;

Siligardi, C .

JOURNAL OF PHYSICAL CHEMISTRY B, 2003, 107 (27) :6519-6525

[5] Reviewing sulfidation corrosion - Yesterday and today [J].

Bornstein, NS .

JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1996, 48 (11) :37-39

[6] The chemistry of sulfidation corrosion - Revisited [J].

Bornstein, NS ;

Allen, WP .

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 :127-134

[7] Role of environmental deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings [J].

Borom, MP ;

Johnson, CA ;

Peluso, LA .

SURFACE & COATINGS TECHNOLOGY, 1996, 86 (1-3) :116-126

[8] Analytical electron microscopy of the mixed zone in NiCoCrAlY-based EB-PVD thermal barrier coatings: as-coated condition versus late stages of TBC lifetime [J].

Braue, W ;

Schulz, U ;

Fritscher, K ;

Leyens, C ;

Wirth, R .

MATERIALS AT HIGH TEMPERATURES, 2005, 22 (3-4) :393-401

[9]

COCKING JA, 1986, HIGH TEMP TECHNOL, V4, P175

[10] CRYSTAL-STRUCTURE AND INFRARED-SPECTRUM OF THE CYCLOSILICATE CA2ZRSI4O12 [J].

COLIN, S ;

DUPRE, B ;

VENTURINI, G ;

MALAMAN, B ;

GLEITZER, C .

JOURNAL OF SOLID STATE CHEMISTRY, 1993, 102 (01) :242-249

← 1 2 3 4 5 6 →