Graphene oxide/hydroxyapatite composite coatings fabricated by electrophoretic nanotechnology for biological applications

被引：258

作者：

Li, Ming ^{[1
]}

Liu, Qian ^{[1
]}

Jia, Zhaojun ^{[1
]}

Xu, Xuchen ^{[1
]}

Cheng, Yan ^{[1
]}

Zheng, Yufeng ^{[1
,2
]}

Xi, Tingfei ^{[1
]}

Wei, Shicheng ^{[1
,3
]}

机构：

[1] Peking Univ, Acad Adv Interdisciplinary Studies, Ctr Biomed Mat & Tissue Engn, Beijing 100871, Peoples R China

[2] Peking Univ, Coll Engn, Dept Mat Sci & Engn, Beijing 100871, Peoples R China

[3] Peking Univ, Sch Stomatol, Dept Oral & Maxillofacial Surg, Beijing 100081, Peoples R China

来源：

CARBON | 2014年 / 67卷

基金：

中国国家自然科学基金; 国家高技术研究发展计划(863计划);

关键词：

TITANIUM SUBSTRATE; GRAPHITE OXIDE; MECHANICAL-PROPERTIES; IN-VITRO; HYDROXYAPATITE; DEPOSITION; NANOCOMPOSITES; LAYER; BIOCOMPATIBILITY; CELLS;

D O I：

10.1016/j.carbon.2013.09.080

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070305 [高分子化学与物理];

摘要：

Graphene oxide (GO) was firstly employed as nanoscale reinforcement fillers in hydroxyapatite (HA) coatings by a cathodic electrophoretic deposition process, and GO/HA coatings were fabricated on pure Ti substrate. The transmission electron microscopy observation and particle size analysis of the suspensions indicated that HA nanoparticles were uniformly decorated on GO sheets, forming a large GO/HA particle group. The addition of GO into HA coatings could reduce the surface cracks and increase the coating adhesion strength from 1.55 +/- 0.39 MPa (pure HA) to 2.75 +/- 0.38 MPa (2 wt.% GO/HA) and 3.3 +/- 0.25 MPa (5 wt.% GO/HA), respectively. Potentiodynamic polarization and electrochemical impedance spectroscopy studies indicated that the GO/HA composite coatings exhibited higher corrosion resistance in comparison with pure HA coatings in simulated body fluid. In addition, superior (around 95% cell viability for 2 wt.% GO/HA) or comparable (80-90% cell viability for 5 wt.% GO/HA) in vitro biocompatibility were observed in comparison with HA coated and uncoated Ti substrate. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：185 / 197

页数：13

共 67 条