Mechanical properties of spark plasma sintered Nb-Al compacts strengthened by dispersion of Nb2N phase and additions of Mo and W

被引：26

作者：

Murakami, T

Komatsu, M

Kitahara, A

Kawahara, M

Takahashi, Y

Ono, Y

机构：

[1] Mech Engn Lab, Tsukuba, Ibaraki 30585654, Japan

[2] AIST, Tosu, Saga 8410052, Japan

[3] Sumitomo Coal Min Co Ltd, Kawasaki, Kanagawa 213, Japan

[4] Oita Ind Res Inst, Oita 87011, Japan

[5] Fukuoka Ind Res Inst, Kitakyushu, Fukuoka 807, Japan

来源：

INTERMETALLICS | 1999年 / 7卷 / 06期

关键词：

niobium aluminides; solid-solution hardening; ternary alloy systems; mechanical alloying and milling; sintering;

D O I：

10.1016/S0966-9795(98)00090-9

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Mechanically alloyed and blended Nb-Al-N powders were sintered by the spark plasma sintering process, and their microstructure and mechanical properties were investigated. All of the Nb-Al-N compacts consisted of phases in the Nb-Al system in which the Nb2N phase was dispersed. The microstructure of blended powder compacts was much coarser than that of mechanically alloyed powder compacts. The compacts obtained by sintering powder produced by crushing blended powder compacts have finer microstructure, higher hardness, and higher fracture toughness than blended powder compacts. The strength of Nb-Al-N compacts increases with increasing the fraction of AlN added to the Nb powder, while their fracture toughness at room temperature decreases. As for the Nb-Al-Mo and Nb-Al-W system, the effect of solid-solution hardening of W was larger than that of Mo, and Nb-15Al-40Mo compact has the highest strength at room temperature and 1273 K among Nb-15Al-xMo compacts. (C) 1999 Elseiver Science Ltd. All rights reserved.

引用

页码：731 / 739

页数：9

共 19 条

[1]

American Society for Metals, 1973, MET HDB MET STRUCT P, V8

[2] NITRIDPHASEN DES NIOBS [J].

BRAUER, G ;

ESSELBORN, R .

ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1961, 309 (3-4) :151-170

[3] HIGH-TEMPERATURE DEFORMATION OF NB3AL ALLOYS [J].

HANADA, S ;

MURAYAMA, Y ;

ABE, Y .

INTERMETALLICS, 1994, 2 (03) :155-165

[4]

HUNT CR, 1968, Z METALLKD, V59, P701

[5] A NEW METALLURGICAL INVESTIGATION OF THE NIOBIUM-ALUMINUM SYSTEM [J].

JORDA, JL ;

FLUKIGER, R ;

MULLER, J .

JOURNAL OF THE LESS-COMMON METALS, 1980, 75 (02) :227-239

[6]

KIMURA M, 1990, P 1 S HIGH PERF MAT, P45

[7] Mechanical milling/alloying of intermetallics [J].

Koch, CC ;

Whittenberger, JD .

INTERMETALLICS, 1996, 4 (05) :339-355

[8] High temperature oxidation of TiAl/SiCp composites manufactured by MA-SPS process [J].

Lee, DB ;

Park, JH ;

Park, YH ;

Kim, YJ .

MATERIALS TRANSACTIONS JIM, 1997, 38 (04) :306-311

[9] INDENTATION FRACTURE-TOUGHNESS OF SINTERED SILICON-CARBIDE IN THE PALMQVIST CRACK REGIME [J].

LI, Z ;

GHOSH, A ;

KOBAYASHI, AS ;

BRADT, RC .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1989, 72 (06) :904-911

[10]

Marshall DB, 1982, J AM CERAM SOC, V65, P175

← 1 2 →