Role of foreign-object damage on thresholds for high-cycle fatigue in Ti-6Al-4V

被引:62
作者
Peters, JO [1 ]
Roder, O
Boyce, BL
Thompson, AW
Ritchie, RO
机构
[1] Univ Calif Berkeley, Dept Mat Sci & Mineral Engn, Berkeley, CA 94720 USA
[2] Daimler Chrysler Aerosp MTU, D-80976 Munich, Germany
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 06期
关键词
D O I
10.1007/s11661-000-0167-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The increasing incidence of military aircraft engine failures that can be traced to high-cycle fatigue (HCF) has prompted a reassessment of the design methodologies for HCF-critical components, such as turbine blades and disks. Because of the high-frequency vibratory loading involved, damage-tolerant design methodologies based on a threshold for no crack growth offer a preferred approach. As impact damage from ingested debris is a prime source of HCF-related failures, the current study is focused on the role of such foreign-object damage (FOD) in influencing fatigue crack-growth thresholds and early crack growth of both large and small cracks in a fan blade alloy, Ti-6Al-4V. FOD, which was simulated by the high-velocity (200 to 300 m/s) impact of steel spheres on a flat surface, was found to reduce markedly the fatigue strength, primarily due to earlier crack initiation. This is discussed in terms of four salient factors: (1) the stress concentration associated with the FOD indentation, (2) the presence of small microcracks in the damaged zone, (3) the localized presence of tensile residual hoop stresses at the base and rim of the indent sites, and (4) microstructural damage from FOD-induced plastic deformation. It was found that no crack growth occurred from FOD impact sites in this alloy at Delta K values below similar to 2.9 MPa root m, i.e., over 50 pct higher than the "closure-free", worst-case threshold value of bK(TH) = 1.9 MPa root m, defined for large cracks in bimodal Ti-6Al-4V alloys at the highest possible load ratio. It is, therefore, concluded that such worst-case, large fatigue crack thresholds can, thus, be used as a practical lower-bound to FOD-initiated cracking in this alloy.
引用
收藏
页码:1571 / 1583
页数:13
相关论文
共 49 条
[1]  
[Anonymous], SHORT FATIGUE CRACKS
[2]  
CHEN X, 1999, 358 ME HARV U
[3]   UTILITY OF SURFACE-FLAWED TENSILE BARS IN CYCLIC LIFE STUDIES [J].
COLES, A ;
JOHNSON, RE ;
POPP, HG .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1976, 98 (04) :305-315
[4]   High cycle fatigue in aircraft gas turbines - An industry perspective [J].
Cowles, BA .
INTERNATIONAL JOURNAL OF FRACTURE, 1996, 80 (2-3) :147-163
[5]   NOTCHED MEMBER FATIGUE LIFE PREDICTIONS COMBINING CRACK INITIATION AND PROPAGATION [J].
DOWLING, NE .
FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1979, 2 (02) :129-138
[6]   PREDICTION OF NON PROPAGATING CRACKS [J].
ELHADDAD, MH ;
TOPPER, TH ;
SMITH, KN .
ENGINEERING FRACTURE MECHANICS, 1979, 11 (03) :573-584
[7]   Microstructure and the development of fatigue cracks at notches [J].
Evans, WJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 263 (02) :160-175
[8]  
EYLON D, 1998, TI6A14V HCFLCF PROGR
[9]  
Frost N.E., 1959, Proc. Inst. Mech. Eng., V173, P811
[10]  
Goodman J., 1930, MECH APPL ENG