A microscopy study of the transition from yielding to crazing in polypropylene

被引:37
作者
Dijkstra, PTS [1 ]
Van Dijk, DJ [1 ]
Huétink, J [1 ]
机构
[1] Univ Twente, Dept Mech Engn, NL-7500 AE Enschede, Netherlands
关键词
D O I
10.1002/pen.10936
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The deformation mechanisms in polypropylene as a function of strain rate have been studied by scanning electron microscopy. Injection molded, dogbone specimens were tested in tension at a temperature of 50degreesC and strain rates from 10(-4) to 90 s(-1). With increasing strain rate a gradual transition from cold drawing and necking to nearly homogeneous deformation was observed. The transition is characterized by a strong elastic recoil after fracture. At (epsilon) over dot = 90 s(-1), the elastic recovery has its maximum value of 70% of the strain at break (epsilon = 0.3). The morphology was studied post mortem at small strains outside the neck using permanganically etched samples. The transition in the macroscopic behavior was found to coincide with a change in the deformation mechanism. Whereas yielding is the dominant mechanism at low strain rates, homogeneous voiding is found at (epsilon) over dot = 90 s(-1). A correlation is suggested between the failure of chain slip within the lamellae and the occurrence of voiding. leading to distinct voiding patterns in the spherulites.
引用
收藏
页码:152 / 160
页数:9
相关论文
共 33 条
[1]   SPHERULITIC MORPHOLOGY OF ISOTACTIC POLYPROPYLENE INVESTIGATED BY SCANNING ELECTRON-MICROSCOPY [J].
ABOULFARAJ, M ;
ULRICH, B ;
DAHOUN, A ;
GSELL, C .
POLYMER, 1993, 34 (23) :4817-4825
[2]   IN-SITU OBSERVATION OF THE PLASTIC-DEFORMATION OF POLYPROPYLENE SPHERULITES UNDER UNIAXIAL TENSION AND SIMPLE SHEAR IN THE SCANNING ELECTRON-MICROSCOPE [J].
ABOULFARAJ, M ;
GSELL, C ;
ULRICH, B ;
DAHOUN, A .
POLYMER, 1995, 36 (04) :731-742
[3]   DIRECT VISUALIZATION OF MICROSTRUCTURAL DEFORMATION PROCESSES IN POLYETHYLENE [J].
ADAMS, WW ;
YANG, D ;
THOMAS, EL .
JOURNAL OF MATERIALS SCIENCE, 1986, 21 (07) :2239-2253
[4]  
Balta-Calleja F. J., 1970, J MACROMOL SCI, V4, P519, DOI [10.1080/00222347008229372, DOI 10.1080/00222347008229372]
[5]   EVOLUTION OF THE CRYSTALLINE TEXTURE OF HIGH-DENSITY POLYETHYLENE DURING UNIAXIAL COMPRESSION [J].
BARTCZAK, Z ;
COHEN, RE ;
ARGON, AS .
MACROMOLECULES, 1992, 25 (18) :4692-4704
[6]   ON THE LAMELLAR MORPHOLOGY OF ISOTACTIC POLYPROPYLENE SPHERULITES [J].
BASSETT, DC ;
OLLEY, RH .
POLYMER, 1984, 25 (07) :935-943
[7]   The influence of inertial effects on the fracture of rapidly loaded compact tension specimens Part A: Loading and fracture initiation [J].
Beguelin, P ;
Fond, C ;
Kausch, HH .
INTERNATIONAL JOURNAL OF FRACTURE, 1998, 89 (01) :85-102
[8]   DEFORMATION MECHANISMS IN CRYSTALLINE POLYMERS [J].
BOWDEN, PB ;
YOUNG, RJ .
JOURNAL OF MATERIALS SCIENCE, 1974, 9 (12) :2034-2051
[9]   Polymers under mechanical stress: Deformation of the nanostructure of isotactic polypropylene revealed by scanning force microscopy [J].
Castelein, G ;
Coulon, G ;
GSell, C .
POLYMER ENGINEERING AND SCIENCE, 1997, 37 (10) :1694-1701
[10]   DILATOMETRIC STUDIES OF POLYMERS UNDERGOING HIGH AND LOW RATE TENSILE DEFORMATION [J].
CESSNA, LC .
POLYMER ENGINEERING AND SCIENCE, 1974, 14 (10) :696-701