On the mechanism of microcrack formation in nanocrystalline Fe-Ni electrodeposits

被引:31
作者
Czerwinski, F [1 ]
Kedzierski, Z [1 ]
机构
[1] STANISLAW STASZIC UNIV MIN & MET, DEPT MET, PL-30059 KRAKOW, POLAND
关键词
D O I
10.1023/A:1018693005002
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The microstructure and internal stress of nanocrystalline Fe-13% Ni alloys electrodeposited onto a steel substrate were examined. A deposit growth was accompanied by the formation of microcracks and a reduction in stress level; during an increase in deposit thickness from 0.1 to 50 mu m, the internal stress decreased from 1450 to 90 MPa. An explanation of crack formation was proposed on the basis of Griffith's theory of fracture. A critical deposit thickness prior to crack propagation, predicted from the mechanism proposed, was in good agreement with the values obtained from in-situ measurements of stress evolution and from direct microscopy observations. The results showed that the thickness of deposits exerted crucial influence on their fracture resistance.
引用
收藏
页码:2957 / 2961
页数:5
相关论文
共 20 条
[1]   MEASUREMENT OF THE ULTIMATE SHEAR-STRENGTH OF A METAL CERAMIC INTERFACE [J].
AGRAWAL, DC ;
RAJ, R .
ACTA METALLURGICA, 1989, 37 (04) :1265-1270
[2]  
American Society for Metals, 1985, MET HDB, V8
[3]  
[Anonymous], 1970, Plating
[4]  
[Anonymous], 1989, DEFORMATION FRACTURE
[5]  
BRENNER A, 1960, ELECTRODEPOSITION AL
[6]  
CHEN JM, 1983, ACTA CHIM SINICA, V41, P1013
[7]   SYNTHESIS OF NANOCRYSTALLINE PERMALLOY BY ELECTRODEPOSITION [J].
CHEUNG, C ;
PALUMBO, G ;
ERB, U .
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (06) :735-740
[8]  
CURRY DA, 1980, MET SCI, V14, P319, DOI 10.1179/030634580790426292
[9]   In-situ measurement of stress generated during electrocrystallization of Fe-Ni alloys [J].
Czerwinski, F .
THIN SOLID FILMS, 1996, 280 (1-2) :199-203
[10]   Grain size internal stress relationship in iron-nickel alloy electrodeposits [J].
Czerwinski, F .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1996, 143 (10) :3327-3332