Influence of ageing on the cold crystallization of glassy poly(ethyleneterephthalate)

被引：32

作者：

Bove, L ^{[1
]}

DAniello, C ^{[1
]}

Gorrasi, G ^{[1
]}

Guadagno, L ^{[1
]}

Vittoria, V ^{[1
]}

机构：

[1] UNIV SALERNO,DIPARTIMENTO INGN CHIM & ALIMENTARE,I-84084 FISCIANO,ITALY

来源：

POLYMER BULLETIN | 1997年 / 38卷 / 05期

关键词：

poly(ethyleneterephthalate); cold crystallization; kinetics of crystallization;

D O I：

10.1007/s002890050091

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The thermal crystallization from the glassy state of different samples of Poly(ethyleneterephthalate) (PET) was investigated with different techniques, such as infrared and x-ray analysis and polarized optical microscopy. The different samples of PET were obtained by ageing the glassy PET films at room temperature and at 60 degrees C; the behaviour of these films was compared with that of the fresh sample, put at the crystallization temperature as soon as prepared. The temperature of crystallization was 120 degrees C. All the techniques, investigated to follow the crystallization phenomenon, show that the fresh sample crystallizes with longer times than the others. This result was correlated with the initial structural organization of the glassy amorphous films.

引用

页码：579 / 585

页数：7

共 26 条

[1] CRYSTALLINITY OF PURE AND NUCLEATED PET [J].

AHARONI, SM ;

SHARMA, RK ;

SZOBOTA, JS ;

VERNICK, DA .

JOURNAL OF APPLIED POLYMER SCIENCE, 1983, 28 (07) :2177-2186

[2]

Alexander L.E., 1969, XRAY DIFFRACTION MET

[3]

BALTACALLEJA FJ, 1993, J POLYM SCI PP, V31, P557

[4] RAPID MEASUREMENTS OF ELASTIC-MODULUS AND DENSITY IN POLYPROPYLENE SHEET DURING AGING [J].

BAUM, JS ;

SCHULTZ, JM .

JOURNAL OF APPLIED POLYMER SCIENCE, 1981, 26 (05) :1579-1584

[5]

Bove L, 1996, J APPL POLYM SCI, V62, P1035, DOI 10.1002/(SICI)1097-4628(19961114)62:7<1035::AID-APP9>3.0.CO

[6]

2-L

[7] MECHANISM OF PHYSICAL AGING IN CRYSTALLINE POLYMERS [J].

CHAI, CK ;

MCCRUM, NG .

POLYMER, 1980, 21 (06) :706-712

[8]

FIELDINGRUSSEL GS, 1970, MAKROMOLEKUL CHEM, V135, P263

[9]

FISCHER EW, 1976, J MATER SCI, V11, P1041, DOI 10.1007/BF02396639

[10]

Geil PH, 1973, POLYM SINGLE CRYSTAL

← 1 2 3 →