Recrystallization texture development in commercial Al-Mn-Mg alloys

被引:175
作者
Daaland, O [1 ]
Nes, E [1 ]
机构
[1] UNIV TRONDHEIM,NORWEGIAN INST TECHNOL,DEPT MET,N-7034 TRONDHEIM,NORWAY
关键词
D O I
10.1016/1359-6454(95)00290-1
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A detailed investigation of the evolution of recrystallization textures during annealing after hot rolling of an Al1Mn1Mg alloy and after hot and cold rolling of an Al1Mn0.5Mg alloy has been carried out, using the EBSP-technique for identification of the individual grain orientations. The growth of grains with a 40 degrees[111] orientation relationship to components in the rolling texture has been followed and compared to the growth of random oriented grains. No oriented growth effect due to an enhanced mobility of 40 degrees[111] boundaries could be detected. However, during low temperature annealing of one of the alloys grains belonging to different texture components were observed to grow at different rates. This special case is associated with a precipitation reaction occurring simultaneously with recrystallization, and the observation is interpreted as a precipitation-induced-effect reflecting that particle stimulated nucleation (PNS) is more sensitive to precipitation than nucleation from the competing 40 degrees[111] sites. In order to illustrate the effect of grains growing at different rates on the structure and texture development, a computer model has been applied for simulating the recrystallization reaction. Reasonable predictions of the kinetics, grain size distribution and final texture (volume fractions) have been obtained.
引用
收藏
页码:1413 / 1435
页数:23
相关论文
共 26 条
[1]  
[Anonymous], PRACTISCHE METALLOGR
[2]  
Daaland O, 1996, ACTA MATER, V44, P1389, DOI 10.1016/1359-6454(95)00289-8
[3]  
DEHOFF RT, 1986, P 7 RIS INT S MET MA, P35
[4]   DIRECT OBSERVATION OF THE DEVELOPMENT OF RECRYSTALLIZATION TEXTURE IN COMMERCIAL PURITY ALUMINUM [J].
DOHERTY, RD ;
KASHYAP, K ;
PANCHANADEESWARAN, S .
ACTA METALLURGICA ET MATERIALIA, 1993, 41 (10) :3029-3053
[5]  
DOHERTY RD, 1962, J I MET, V91, P332
[6]  
DUGGAN BJ, 1993, ACTA METALL MATER, V42, P1921
[7]  
FURU T, 1990, MATER SCI TECH SER, V6, P1093, DOI 10.1179/026708390790189957
[8]   ESTIMATION OF NUCLEATION RATE AND GROWTH-RATE FROM TIME-DEPENDENCE OF GLOBAL MICROSTRUCTURAL PROPERTIES DURING PHASE-TRANSFORMATIONS [J].
GOKHALE, AM ;
DEHOFF, RT .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (04) :559-564
[9]  
HILLIARD JE, 1966, RECRYSTALLIZATION GR, P267
[10]   MECHANISM OF DEFORMATION AND DEVELOPMENT OF ROLLING TEXTURES IN POLYCRYSTALLINE FCC METALS .2. SIMULATION AND INTERPRETATION OF EXPERIMENTS ON THE BASIS OF TAYLOR-TYPE THEORIES [J].
HIRSCH, J ;
LUCKE, K .
ACTA METALLURGICA, 1988, 36 (11) :2883-2904