Influence of plasma spray parameters on mechanical properties of yttria stabilized zirconia coatings. II: Acoustic emission response

被引：51

作者：

Kucuk, A ^{[1
]}

Berndt, CC ^{[1
]}

Senturk, U ^{[1
]}

Lima, RS ^{[1
]}

机构：

[1] SUNY Stony Brook, Dept Mat Sci & Engn, Ctr Thermal Spray Res, Stony Brook, NY 11794 USA

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2000年 / 284卷 / 1-2期

关键词：

thermal barrier coatings; acoustic emission; cracking behavior;

D O I：

10.1016/S0921-5093(00)00800-5

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Yttria (8 wt.%) stabilized zirconia (YSZ) with a NiCrAlY bond coat was atmospherically plasma sprayed on mild steel substrates using various processing parameters including YSZ coating thickness, bond coat thickness, stand off distance, and substrate temperature. The cracking behavior of these coatings under four point bending load was examined using an acoustic emission (AE) recorder. The numbers of AE events exhibited during the elastic and plastic deformation of coatings were analyzed. Using multi-linear regression analysis, the number of AE events was correlated to the spray parameters. This analysis revealed that coatings with thicker YSZ top coat and NiCrYAl bond coat sprayed on a heated substrate at shorter stand off distance exhibited more AE activity and released higher AE energy under the bending. The greater emission activity and higher AE energy were evidence of severe cracking. (C) 2000 Elsevier Science S.A. All rights reserved.

引用

页码：41 / 50

页数：10

共 25 条

[1]

Berndt C.C., 1988, MAT SCI FORUM, V34-36, P457

[2] ACOUSTIC-EMISSION EVALUATION OF PLASMA-SPRAYED THERMAL BARRIER COATINGS [J].

BERNDT, CC .

JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 1985, 107 (01) :142-146

[3]

BERNDT CC, 1984, MECH ENG, V106, P85

[4]

BERNDT CC, 1983, 10 INT THERM SPRAY C

[5]

BIANCHI L, 1997, THERMAL SPRAY, P831

[6]

BOCH P, 1984, ADV CERAM, V12, P488

[7]

David Kingery W., 1976, INTRO CERAMICS, V17

[8] THROUGH-THICKNESS RESIDUAL-STRESS EVALUATIONS FOR SEVERAL INDUSTRIAL THERMAL SPRAY COATINGS USING A MODIFIED LAYER-REMOVAL METHOD [J].

GREVING, DJ ;

RYBICKI, EF ;

SHADLEY, JR .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1994, 3 (04) :379-388

[9] EFFECTS OF COATING THICKNESS AND RESIDUAL-STRESSES ON THE BOND STRENGTH OF ASTM C633-79 THERMAL SPRAY COATING TEST SPECIMENS [J].

GREVING, DJ ;

SHADLEY, JR ;

RYBICKI, EF .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1994, 3 (04) :371-378

[10]

ILAVKY J, 1996, 9 NAT THRM SPRAY C A, P725

← 1 2 3 →