Pseudo float melting state in ladle arc-melt-type furnace for preparing crystalline inclusion-free bulk amorphous alloy

被引：75

作者：

Yokoyama, Y ^{[1
]}

Inoue, K ^{[1
]}

Fukaura, K ^{[1
]}

机构：

[1] Himeji Inst Technol, Fac Engn, Himeji, Hyogo 6712201, Japan

来源：

MATERIALS TRANSACTIONS | 2002年 / 43卷 / 09期

关键词：

perfect melting; Zr50CU30Ni10Al10 bulk amorphous alloy; ladle-type arc-melting method; squeeze casting;

D O I：

10.2320/matertrans.43.2316

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A homogeneous melting state without any crystalline inclusions was achieved in an are melt furnace by using a ladle arc-melting-type furnace. Molten alloy for pouring can be melted completely by are heating just above the mold in a pseudo float melting (PFM) state. We combined a ladle arc-melt-type furnace and the squeeze cast method to produce bulk amorphous alloy sheet with a single amorphous phase structure, thereby successfully producing crystalline inclusion-free Zr50Cu30Ni10Al10 bulk amorphous alloy sheets. The tensile strengths of the Zr50Cu30Ni10Al10 bulk amorphous alloys exceeded 1800 MPa, and the bending deflection of the alloys was improved by a factor of 10 using the PFM process.

引用

页码：2316 / 2319

页数：4

共 16 条

[1] Effects of overload and frequency on fatigue crack propagation in nanocrystalline Zr-based bulk metallic glass [J].

Fujita, K ;

Inoue, A ;

Zhang, T .

MATERIALS TRANSACTIONS, 2001, 42 (08) :1502-1508

[2] Fatigue crack propagation in a nanocrystalline Zr-based bulk metallic glass [J].

Fujita, K ;

Inoue, A ;

Zhang, T .

MATERIALS TRANSACTIONS JIM, 2000, 41 (11) :1448-1453

[3] Fracture toughness and fatigue-crack propagation in a Zr-Ti-Ni-Cu-Be bulk metallic glass [J].

Gilbert, CJ ;

Ritchie, RO ;

Johnson, WL .

APPLIED PHYSICS LETTERS, 1997, 71 (04) :476-478

[4] FABRICATION OF BULKY ZR-BASED GLASSY ALLOYS BY SUCTION CASTING INTO COPPER MOLD [J].

INOUE, A ;

ZHANG, T .

MATERIALS TRANSACTIONS JIM, 1995, 36 (09) :1184-1187

[5] Effect of additional elements on glass transition behavior and glass formation tendency of Zr-Al-Cu-Ni alloys [J].

Inoue, A ;

Shibata, T ;

Zhang, T .

MATERIALS TRANSACTIONS JIM, 1995, 36 (12) :1420-1426

[6] Impact fracture energy of bulk amorphous Zr55Al10Cu30Ni5 alloy [J].

Inoue, A ;

Zhang, T .

MATERIALS TRANSACTIONS JIM, 1996, 37 (11) :1726-1729

[7]

INOUE A, 2002, MATER T JIM, V43, P571

[8]

Inoue A., 1998, BULK AMORPHOUS ALLOY

[9] Application of Zr-based bulk glassy alloys to golf clubs [J].

Kakiuchi, H ;

Inoue, A ;

Onuki, M ;

Takano, Y ;

Yamaguchi, T .

MATERIALS TRANSACTIONS, 2001, 42 (04) :678-681

[10]

Markiv VY, 1970, POWDER METALL MET C+, V12, P53

← 1 2 →