Hot isostatic pressing of TiB2-ZrO2(2mol% Y2O3) composite powders

被引：33

作者：

Muraoka, Y ^{[1
]}

Yoshinaka, M ^{[1
]}

Hirota, K ^{[1
]}

Yamaguchi, O ^{[1
]}

机构：

[1] DOSHISHA UNIV,FAC ENGN,DEPT MOLEC SCI & TECHNOL,TANABE,KYOTO 61003,JAPAN

来源：

MATERIALS RESEARCH BULLETIN | 1996年 / 31卷 / 07期

关键词：

intermetallic compounds; oxides; mechanical properties;

D O I：

10.1016/0025-5408(96)00069-4

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Dense sintered composites of TiB2 and ZrO2(2 mol% Y2O3) have been fabricated by hot isostatic pressing for 2 h at 1500 degrees C under 196 MPa. The ZrO2 particles in the composites consist of m- >> t-ZrO2. There is no reaction between TiB2 and ZrO2. Microstructures and mechanical properties are examined, in connection with increased ZrO2 content. The fracture toughness and bending strength of the composites with 30 mol% ZrO2 content are 11.2 MPa . m(1/2) and 680 MPa, respectively.

引用

页码：787 / 792

页数：6

共 9 条

[1]

DOYAMA M, 1989, DATA HDB INTERMETALL, P31

[2] FRACTURE TOUGHNESS DETERMINATIONS BY INDENTATION [J].

EVANS, AG ;

CHARLES, EA .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1976, 59 (7-8) :371-372

[3]

EVANS AG, 1984, J AM CERAM SOC, V67, P255, DOI 10.1111/j.1151-2916.1984.tb18842.x

[4] PHASE ANALYSIS IN ZIRCONIA SYSTEMS [J].

GARVIE, RC .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1972, 55 (06) :303-&

[5]

HORI S, 1990, TOUGHENING ZIRCONIA, P139

[6] LATTICE-PARAMETERS AND DENSITY FOR Y2O3-STABILIZED ZRO2 [J].

INGEL, RP ;

LEWIS, D .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1986, 69 (04) :325-332

[7] MECHANICS OF TRANSFORMATION-TOUGHENING IN BRITTLE MATERIALS [J].

MCMEEKING, RM ;

EVANS, AG .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1982, 65 (05) :242-246

[8]

NIIHARA K, 1984, J AM CERAM SOC, V67, pC13

[9]

WATANABE T, 1985, J AM CERAM SOC, V68, pC34

← 1 →