Preparation of nanoscaled BaTiO3 powders by DSS method near room temperature under normal pressure

被引：44

作者：

Qi, HQ ^{[1
]}

Li, LT ^{[1
]}

Wang, YL ^{[1
]}

Gui, ZL ^{[1
]}

机构：

[1] Tsing Hua Univ, Dept Mat Sci & Engn, Beijing 100084, Peoples R China

来源：

JOURNAL OF CRYSTAL GROWTH | 2004年 / 260卷 / 3-4期

关键词：

growth from solutions; BaTiO3; nanoscaled powder;

D O I：

10.1016/j.jcrysgro.2003.08.059

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

A new method of direct synthesis nano-BaTiO3 Powders from solution was developed in this study. Dissolving Ba(OH)(2) (.) 8H(2)O into water as base solution, nanocrystalline BaTiO3 powders can be obtained by mixing ethanol solution of tetrabutyl titanate with hot base solution under normal pressure. When the temperature of the base solution was 60 degreesC, we obtained crystalline powders with average particle size of about 25 nm. The activity of the powders can be held up because the calcination at high temperature is not necessary using this method. (C) 2003 Elsevier B.V. All rights reserved.

引用

页码：551 / 556

页数：6

共 7 条

[1]

ATKINS PW, 1982, PHYSICAL CHEM, P1002

[2] LATTICE-DYNAMICS AND ORIGIN OF FERROELECTRICITY IN BATIO3 - LINEARIZED-AUGMENTED-PLANE-WAVE TOTAL-ENERGY CALCULATIONS [J].

COHEN, RE ;

KRAKAUER, H .

PHYSICAL REVIEW B, 1990, 42 (10) :6416-6423

[3] HYDROTHERMAL SYNTHESIS OF BARIUM-TITANATE FINE PARTICLES FROM AMORPHOUS AND CRYSTALLINE TITANIA [J].

KUMAZAWA, H ;

ANNEN, S ;

SADA, E .

JOURNAL OF MATERIALS SCIENCE, 1995, 30 (18) :4740-4744

[4]

QI JQ, 2002, Patent No. 02153870

[5] SIZE DRIVEN PHASE-TRANSITION IN NANOCRYSTALLINE BATIO3 [J].

SCHLAG, S ;

EICKE, HF .

SOLID STATE COMMUNICATIONS, 1994, 91 (11) :883-887

[6] The hydrothermal synthesis of BaTiO3 fine particles from hydroxide-alkoxide precursors [J].

Urek, S ;

Drofenik, M .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1998, 18 (04) :279-286

[7] Preparation of nm-sized BaTiO3 crystallites by a LTDS method using a highly concentrated aqueous solution [J].

Wada, S ;

Tsurumi, T ;

Chikamori, H ;

Noma, T ;

Suzuki, T .

JOURNAL OF CRYSTAL GROWTH, 2001, 229 (01) :433-439

← 1 →