Surface modification of TiNi alloy through tantalum immersion ion implantation

被引:33
作者
Cheng, Y [1 ]
Wei, C [1 ]
Gan, KY [1 ]
Zhao, LC [1 ]
机构
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
关键词
plasma immersion ion implantation; corrosion resistance; tantalum; TiNi alloy;
D O I
10.1016/S0257-8972(03)00745-X
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
TiNi alloy samples were implanted with tantalum at a dose of 3.1 X 10(17) N/cm(2) by means of Plasma immersion ion implantation WHO method. The surface morphology, chemical composition was characterized by Atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The corrosion resistance, were determined by electrochemical methods in 0.9% NaCl solution at 37 degreesC. The results show that PIII treatment can increase the open-circuit corrosion potential (E-corr) and decrease the corrosion current density (I-corr). The pitting potential (E-br) for the tantalum implanted TiNi alloy is approximately 810 mV, more than 200 mV higher than that of the unimplanted one. The corrosion hystersis loop of the unimplanted TiNi alloy is larger than that of the implanted material, indicating improvement of the repassivating ability and pitting resistance of the TiNi alloys. (C) 2003 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:261 / 265
页数:5
相关论文
共 22 条
[1]  
BINCH JG, 1999, P 1 EUR C SHAP MEM S, P154
[2]   An overview of nitinol medical applications [J].
Duerig, T ;
Pelton, A ;
Stöckel, D .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 273 :149-160
[3]  
ENDO K, 1994, P 1 INT C SHAP MEM S, P197
[4]   Corrosion resistance of N-, Cr- or Cr+N-implanted AISI 420 stainless steel [J].
Hirvonen, J-P. ;
Rueck, D. ;
Yan, S. ;
Mahiout, A. ;
Torri, P. ;
Likonen, J. .
SURFACE & COATINGS TECHNOLOGY, 1995, 74-75 (1-3) :760-764
[5]  
Jia WY, 1999, J BIOMED MATER RES, V48, P488, DOI 10.1002/(SICI)1097-4636(1999)48:4<488::AID-JBM14>3.0.CO
[6]  
2-D
[7]   Passivation of nitinol wire for vascular implants - a demonstration of the benefits [J].
O'Brien, B ;
Carroll, WM ;
Kelly, MJ .
BIOMATERIALS, 2002, 23 (08) :1739-1748
[8]  
PHILIPPE P, 1999, P 1 EUR C SHAP MEM S, P165
[9]   Localized corrosion behaviour in simulated human body fluids of commercial Ni-Ti orthodontic wires [J].
Rondelli, G ;
Vicentini, B .
BIOMATERIALS, 1999, 20 (08) :785-792
[10]   SURFACE SPECTROSCOPIC CHARACTERIZATION OF TINI NEARLY EQUIATOMIC SHAPE-MEMORY ALLOYS FOR IMPLANTS [J].
SHABALOVSKAYA, SA ;
ANDEREGG, JW .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1995, 13 (05) :2624-2632