Experimental study on AC losses in Ag sheathed PbBi2223 tapes with twist filaments

Experimental measurements of AC losses were carried out on Ag sheathed PbBi2223 tapes with twisted and untwisted filaments. Losses were measured at 77 K as function of frequency and magnetic field parallel and perpendicular to the tape surface, using appropriate pick-up loops. Both the first and third harmonics of the signal were measured, in order to distinguish between the hysteresis loss and other types of loss. The effect of filaments uncoupling by twisting was clearly identified. For a tape with a twist pitch of 10 mm and I-c = 40 A (similar to 20 kA cm(-2)) operating at 43 Hz, the filaments are uncoupled in fields less than 40 mT, which is greater than the full penetration field for both the filaments and the tape. Hence, a reduction in the hysteretic loss of the superconducting core is realised at power frequency between 10 and 40 mT. Results form the self-field loss measurement implies the uncoupling of twisted filaments at relative low transport current (I < 0.5I(c)) (C) 1998 Elsevier Science B.V. All rights reserved.