Cation self-diffusion of 44Ca, 88Y, and 96Zr in single-crystalline calcia- and yttria-doped zirconia

被引:93
作者
Kilo, M
Taylor, MA
Argirusis, C
Borchardt, G
Lesage, B
Weber, S
Scherrer, S
Scherrer, H
Schroeder, M
Martin, M
机构
[1] Tech Univ Clausthal, Inst Met, D-38678 Clausthal Zellerfeld, Germany
[2] Univ Paris 11, LEMHE, CNRS, ESA 8072, F-91405 Orsay, France
[3] Ecole Mines, Phys Mat Lab, F-54042 Nancy, France
[4] Rhein Westfal TH Aachen, Inst Phys Chem, D-52062 Aachen, Germany
关键词
D O I
10.1063/1.1628379
中图分类号
O59 [应用物理学];
学科分类号
摘要
Self-diffusion of calcium, yttrium, and zirconium in single-crystalline YSZ and CSZ (YSZ: yttria-stabilized zirconia; containing 10 to 32 mol % Y2O3; CSZ: calcia-stabilized zirconia; containing 11 and 17 mol % CaO) was measured at temperatures between 960 and 1700 degreesC. For zirconium and calcium diffusion, the stable isotopes Ca-44 and Zr-96 were used as tracers and the samples were analyzed with secondary ion mass spectrometry. In the case of yttrium diffusion, the radioactive tracer Y-88 was used and an abrasive sectioning technique was applied. Zirconium bulk diffusion is slower than yttrium and calcium bulk diffusion, and there is a nearly linear correlation of diffusion coefficient with cation radius. In YSZ, zirconium and yttrium bulk diffusivity are maximum for a stabilizer content of 10-11 mol %, while in CSZ both calcium and zirconium tracer diffusion are independent of the calcium content. The activation enthalpy of yttrium stabilizer bulk diffusion (4.2 eV) is, as in CSZ, slightly smaller than for zirconium bulk diffusion (4.5 eV). The yttrium dislocation pipe diffusivity is five to six orders of magnitude faster than the bulk diffusivity, and its activation enthalpy (3.5 eV) is also smaller than that of the bulk diffusion. From the activation enthalpy and from the concentration dependence of the cation bulk diffusion, it is concluded that the cation diffusion occurs either via free vacancies (V-Zr(4)' in YSZ) or via bound vacancies ([V-Zr(4)'-2V(O)(2.)](x) in CSZ). (C) 2003 American Institute of Physics.
引用
收藏
页码:7547 / 7552
页数:6
相关论文
共 30 条
[1]   ZIRCONIA-BASED SOLID ELECTROLYTES - MICROSTRUCTURE, STABILITY AND IONIC-CONDUCTIVITY [J].
BADWAL, SPS .
SOLID STATE IONICS, 1992, 52 (1-3) :23-32
[2]   Grain boundary diffusion of magnesium in zirconia [J].
Bak, T ;
Nowotny, J ;
Prince, K ;
Rekas, M ;
Sorrell, CC .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2002, 85 (09) :2244-2250
[3]   KINETIC DEMIXING AND DECOMPOSITION OF MULTICOMPONENT OXIDES DUE TO A NONHYDROSTATIC STRESS [J].
DIMOS, D ;
WOLFENSTINE, J ;
KOHLSTEDT, DL .
ACTA METALLURGICA, 1988, 36 (06) :1543-1552
[4]   DISLOCATION VELOCITIES IN CUBIC ZIRCONIA (ZRO2) SINGLE-CRYSTALS [J].
FARBER, BY ;
CHIARELLI, AS ;
HEUER, AH .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1995, 72 (01) :59-80
[5]  
Gall M.L., 1994, PHILOS MAG A, V70, P761
[6]  
HERZIG C, 1998, DIFFUSION CONDENSED, P90
[7]  
Kaur I., 1995, Fundamentals of Grain and Interphase Boundary Diffusion, VThird
[8]  
Kilo M, 1999, ELEC SOC S, V99, P228
[9]  
Kilo M, 2003, ELEC SOC S, V2003, P214
[10]   Computer modelling of ion migration in zirconia [J].
Kilo, M ;
Jackson, RA ;
Borchardt, G .
PHILOSOPHICAL MAGAZINE, 2003, 83 (29) :3309-3325