Hydroxyapatite coating by dipping method, and bone bonding strength

Hydroxyapatite (HA) was coated onto titanium rods by a dip coating method using HA sol. The HA sols were prepared by dispersing HA crystals less than 100 nm length in distilled water or physiological salt solution using an ultrasonic homogenizer. The surface of the HA coating was homogeneous as determined by scanning electron microscopy (SEM). After im plantation of uncoated and HA dip coated titanium rods in dog femurs, new bone formation was observed only around the coated material. The bone bonding strength to HA coated rods was 1.0, 1.5, 2.0 and 2.5 Mpa after 1,2,3 and 4 weeks implantation, respectively, as determined by pull-out testing. These values were over twice that of the uncoated titanium rods at 1-4 weeks after im plantation. The dip coated titanium exhibited superior biocompatibility to the uncoated implant and may be of great value for bone repacement applications.