Corrosion behavior of intermetallic compound of TiAl-5Nb in molten LiCl-Li2O

被引：14

作者：

Gao, Q ^{[1
]}

Liu, RY

Zhang, JS

Guo, JT

机构：

[1] Dalian Univ Technol, Dept Mat Engn, Dalian 116024, Peoples R China

[2] Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China

来源：

MATERIALS LETTERS | 2005年 / 59卷 / 16期

关键词：

TiAl-5Nb; molten LiCI-Li2O; corrosion;

D O I：

10.1016/j.matlet.2005.02.015

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The corrosion behavior of TiAl-5Nb intermetallic compound was investigated in molten LiCl-Li2O with immersion experiment in air at 750 degrees C. TiAl-5Nb showed much better corrosion resistance in molten LiCI-Li2O than 310SS stainless steel. TiAl-5Nb exhibited a fast weight loss at the initial stage of corrosion, and then the weight loss stabilized as a slow corrosion rate. The corrosion scale show a bilayered structure: the outer layer is composed of large grains of gamma-LiAlO2, whereas the inner layer is a compact titanium oxide-rich (Li-2 TiO3, TiO2) layer. The fast corrosion at the beginning of corrosion is due to the fast growth of gamma-LiAlO2, and the slower corrosion rate at the latter stage of corrosion is owing to the formation of protective inner layer of titanium oxides (Li2TiO3, TiO2). (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：2052 / 2058

页数：7

共 17 条

[1] Behavior of titanium species in molten Li2CO3-Na2CO3 and Li2CO3-K2CO3 under anodic and cathodic conditions.: I -: Thermodynamic predictions at 550-750°C [J].

Chauvaut, V ;

Cassir, M ;

Denos, Y .

ELECTROCHIMICA ACTA, 1998, 43 (14-15) :1991-2003

[2]

CHO SH, 2000, KOREAN J MAT RES, V10, P471

[3]

CHO SH, 1999, KOREAN J MAT RES, V9, P556

[4] THE EFFECTS OF CHLORIDES, HYDROGEN-CHLORIDE, AND SULFUR-DIOXIDE IN THE OXIDATION OF STEELS BELOW DEPOSITS [J].

GRABKE, HJ ;

REESE, E ;

SPIEGEL, M .

CORROSION SCIENCE, 1995, 37 (07) :1023-1043

[5]

GUAN C, 2000, CORROS SCI PROT TECH, V12, P134

[6] PLASTIC-DEFORMATION AND FRACTURE OF BINARY TIAL-BASE ALLOYS [J].

HUANG, SC ;

HALL, EL .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02) :427-439

[7] Corrosion performance of ferrous and refractory metals in molten salts under reducing conditions [J].

Indacochea, JE ;

Smith, JL ;

Litko, KR ;

Karell, EJ .

JOURNAL OF MATERIALS RESEARCH, 1999, 14 (05) :1990-1995

[8] High-temperature oxidation and corrosion of structural materials in molten chlorides [J].

Indacochea, JE ;

Smith, JL ;

Litko, KR ;

Karell, EJ ;

Raraz, AG .

OXIDATION OF METALS, 2001, 55 (1-2) :1-16

[9]

KIM YW, 1995, JOM-J MIN MET MAT S, V47, P38

[10] IGNITION OF NICKEL IN ENVIRONMENTS CONTAINING OXYGEN AND CHLORINE [J].

LEE, YY ;

MCNALLAN, MJ .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (06) :1099-1107

← 1 2 →