Thermal stability of sputtered tungsten carbide as diffusion barrier for copper metallization

被引:27
作者
Wang, SJ [1 ]
Tsai, HY
Sun, SC
Shiao, MH
机构
[1] Natl Cheng Kung Univ, Dept Elect Engn, Inst Microelect, Tainan, Taiwan
[2] Wafertech, Res & Dev, Camas, WA 98607 USA
[3] Natl Chunghsing Univ, Inst Mat Engn, Taichung, Taiwan
关键词
D O I
10.1149/1.1386644
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
This work investigated the thermal stability, of tungsten carbide (WCx) films deposited by a sputtering process with a WC target as diffusion barrier layer between Cu and Si. The as-deposited WCx film has a nanocrystalline structure and a low electrical resistivity of around 227 mu Omega cm. Film characterization reveals that the WCx film was able to preserve the integrity of the Cu (2000 Angstrom)/WCx (500 Angstrom)/n-Si structure without formation of Cu3Si, up to a 600 degreesC annealing for 30 min. In addition, diode leakage current measurements on the same contact structure, but with a p(+)n-Si substrate did not show deterioration of electrical characteristics up to a 550 degreesC annealing. As. the thickness of the WCx barrier was reduced to 150 Angstrom, the WCx film retained the integrity of diodes up to 500 degreesC without increasing the diode leakage current. The failure of WCx film after high temperature annealing is attributed to the Cu diffusion into the Si substrate through grain boundaries or local defects of the WCx barrier layer, in which some local defects may arise from the formation of W5Si3. (C) 2001 The Electrochemical Society.
引用
收藏
页码:G500 / G506
页数:7
相关论文
共 26 条
[1]   ROOM-TEMPERATURE EPITAXY OF CU ON SI(111) USING PARTIALLY IONIZED BEAM DEPOSITION [J].
BAI, P ;
YANG, GR ;
YOU, L ;
LU, TM ;
KNORR, DB .
JOURNAL OF MATERIALS RESEARCH, 1990, 5 (05) :989-997
[2]   Investigation of copper metallization induced failure of diode structures with and without a barrier layer [J].
Baumann, J ;
Kaufmann, C ;
Rennau, M ;
Werner, T ;
Gessner, T .
MICROELECTRONIC ENGINEERING, 1997, 33 (1-4) :283-291
[3]  
de Boer F.R., 1988, COHESION METALS TRAN
[4]   DIFFUSION BARRIER PERFORMANCE OF PULSED LASER DEPOSITED AMORPHOUS TUNGSTEN CARBIDE FILMS [J].
GHAISAS, S .
JOURNAL OF APPLIED PHYSICS, 1991, 70 (12) :7626-7628
[5]   TANTALUM AS A DIFFUSION BARRIER BETWEEN COPPER AND SILICON - FAILURE MECHANISM AND EFFECT OF NITROGEN ADDITIONS [J].
HOLLOWAY, K ;
FRYER, PM ;
CABRAL, C ;
HARPER, JME ;
BAILEY, PJ ;
KELLEHER, KH .
JOURNAL OF APPLIED PHYSICS, 1992, 71 (11) :5433-5444
[6]   TANTALUM AS A DIFFUSION BARRIER BETWEEN COPPER AND SILICON [J].
HOLLOWAY, K ;
FRYER, PM .
APPLIED PHYSICS LETTERS, 1990, 57 (17) :1736-1738
[7]   Diffusion barrier properties of TaC between Si and Cu [J].
Imahori, J ;
Oku, T ;
Murakami, M .
THIN SOLID FILMS, 1997, 301 (1-2) :142-148
[8]   TANTALUM-BASED DIFFUSION-BARRIERS IN SI/CU VLSI METALLIZATIONS [J].
KOLAWA, E ;
CHEN, JS ;
REID, JS ;
POKELA, PJ ;
NICOLET, MA .
JOURNAL OF APPLIED PHYSICS, 1991, 70 (03) :1369-1373
[9]   MICROSTRUCTURAL DEPENDENCE OF ANNEALING TEMPERATURE IN MAGNETRON-SPUTTERED AL-SI-CU FILMS [J].
LIANG, MK ;
LING, YC .
JOURNAL OF APPLIED PHYSICS, 1993, 74 (06) :3890-3898
[10]   CATALYTIC-OXIDATION OF (001)SI IN THE PRESENCE OF CU3SI AT ROOM-TEMPERATURE [J].
LIU, CS ;
CHEN, LJ .
JOURNAL OF APPLIED PHYSICS, 1993, 74 (05) :3611-3613