Surface reactions on beryllium after carbon vapour deposition and thermal treatment

被引：22

作者：

Goldstrass, P ^{[1
]}

Klages, KU ^{[1
]}

Linsmeier, C ^{[1
]}

机构：

[1] EURATOM Assoc, Max Planck Inst Plasmaphys, D-85748 Garching, Germany

来源：

JOURNAL OF NUCLEAR MATERIALS | 2001年 / 290卷

关键词：

beryllium; carbon; beryllium carbide; material mixing;

D O I：

10.1016/S0022-3115(00)00617-6

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Surface reactions and carbon layer formation on clean metallic beryllium are investigated in situ by X-ray photoelectron spectroscopy (XPS) and Rutherford backscattering spectroscopy (RBS). The carbon is supplied by an electron beam evaporation device. The deposited films are successively heated to temperatures between 373 and 873 K in steps of 100 K and analysed after each step. After deposition at room temperature an amount of Be2C up to 6 x 10(15) cm(-2) is present at the beryllium/carbon interface with elementary carbon on top. A first additional carbide formation takes place after heating to 473 K. For deposited amounts below 5 x 10(16) cm(-2) almost all carbon has reacted to carbide after the 673 K step. The carbidisation is complete at 773 K. Applying annealing times between 10 and 30 min characteristic Be2C amounts build up for each temperature. Carbon diffusion into the bulk beryllium does not take place for temperatures below 773 K. (C) 2001 Elsevier Science B.V. All rights reserved.

引用

页码：76 / 79

页数：4

共 14 条

[1] Hydrogen isotope retention in beryllium for tokamak plasma-facing applications [J].

Anderl, RA ;

Causey, RA ;

Davis, JW ;

Doerner, RP ;

Federici, G ;

Haasz, AA ;

Longhurst, GR ;

Wampler, WR ;

Wilson, KL .

JOURNAL OF NUCLEAR MATERIALS, 1999, 273 (01) :1-26

[2] Release of hydrogen from co-existing layers of carbon and beryllium with vacuum heating [J].

Ashida, K ;

Watanabe, K ;

Okabe, T .

JOURNAL OF NUCLEAR MATERIALS, 1997, 241 :1060-1064

[3] IMPACT OF JET EXPERIMENTAL RESULTS AND ENGINEERING DEVELOPMENT ON THE DEFINITION OF THE ITER DESIGN CONCEPT [J].

BERTOLINI, E .

FUSION ENGINEERING AND DESIGN, 1995, 27 :27-38

[4] Combined ion and electron spectroscopy study of the surface reactions of beryllium with carbon [J].

Goldstrass, P ;

Linsmeier, C .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2000, 161 :411-414

[5]

Hultgren R. R., 1973, SELECTED VALUES THER

[6]

*ITER PROJ, 1996, 1L IDOMSG ITER PROJ

[7]

LINSMEIER C, UNPUB PHYSICA SCRIPT

[8]

NIEH T, 1986, SCRIPTA METALL, P87

[9]

REBUT P, 1985, JETR8503 JOINT UND

[10] Early stages of carbon film growth: carbide interface formation on molybdenum [J].

Reinke, P ;

Oelhafen, P .

← 1 2 →