Using nanoemeraldine salt-polyaniline for preparation of a new anticorrosive water-based epoxy coating

被引：149

作者：

Bagherzadeh, M. R. ^{[1
]}

Mahdavi, F. ^{[1
]}

Ghasemi, M. ^{[1
]}

Shariatpanahi, H. ^{[1
]}

Faridi, H. R. ^{[2
]}

机构：

[1] NIOC, Res Inst Petr Ind, Ind & Environm Protect Res Div, Coating Res Ctr, Tehran, Iran

[2] NIOC, Res Inst Petr Ind, Ind & Environm Protect Res Div, Corros Dept, Tehran, Iran

来源：

PROGRESS IN ORGANIC COATINGS | 2010年 / 68卷 / 04期

关键词：

Conductive polymers; Water-based epoxy; Anticorrosive coating; Nanopolyaniline; Aminic hardener; Emeraldine salt; CORROSION PROTECTION; ORGANIC COATINGS; EMERALDINE BASE; STEEL; POLYMERS; PAINT; COMPOSITES; ADDITIVES; PIGMENTS; METALS;

D O I：

10.1016/j.porgcoat.2010.03.005

中图分类号：

O69 [应用化学];

学科分类号：

070301 [无机化学];

摘要：

In this study the anticorrosion performance of a two components water-based epoxy coating system is improved by using the nanopolyaniline (nanoPAni) particles. The purchased nanopolyaniline which was dispersed in water was mixed mechanically with the water-based polyamidoamine hardener of the epoxy system using ultrasonic homogenizer. Average particle size of the polyaniline in hardener was determined using dynamic light scattering technique (DLS). Results revealed that the particles were in the range of 50-57 nm. After combining the prepared sample with the DGEBA epoxy resin, finished coating was applied on steel substrates. Anticorrosion performance and adhesion properties of coating which contained nanoPAni were compared to the model water-based epoxy coating with the help of salt spray and adhesion tests. Results showed that anticorrosive performance of the model water-based epoxy system improved dramatically by adding only 0.02 wt.% nanoPAni. However in contrast to model coating, adherence of PAni-epoxy coating to steel plates was remained constant after their exposure to the corrosive media. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：319 / 322

页数：4

共 18 条

[1]

Corrosion inhibition of steel in sodium chloride solution by undoped polyaniline epoxy blend coating [J].

Akbarinezhad, E. ;

Ebrahimi, M. ;

Faridi, H. R. .

PROGRESS IN ORGANIC COATINGS, 2009, 64 (04) :361-364

[2]

Corrosion protection with polyaniline and polypyrrole as anticorrosive additives for epoxy paint [J].

Armelin, Elaine ;

Pla, Rosa ;

Liesa, Francisco ;

Ramis, Xavier ;

Iribarren, Jose I. ;

Aleman, Carlos .

CORROSION SCIENCE, 2008, 50 (03) :721-728

[3]

Marine paint fomulations:: Conducting polymers as anticorrosive additives [J].

Armelin, Elaine ;

Oliver, Ramon ;

Liesa, Francisco ;

Iribarren, Jose I. ;

Estrany, Francesc ;

Aleman, Carlos .

PROGRESS IN ORGANIC COATINGS, 2007, 59 (01) :46-52

[4]

Study of epoxy and alkyd coatings modified with emeraldine base form of polyaniline [J].

Armelin, Elaine ;

Ocampo, Cintia ;

Liesa, Francisco ;

Iribarren, Jose Ignacio ;

Ramis, Xavier ;

Aleman, Carlos .

PROGRESS IN ORGANIC COATINGS, 2007, 58 (04) :316-322

[5]

Anticorrosion performances of epoxy coatings modified with polyaniline: A comparison between the emeraldine base and salt forms [J].

Armelin, Elaine ;

Aleman, Carlos ;

Iribarren, Jose Ignacio .

PROGRESS IN ORGANIC COATINGS, 2009, 65 (01) :88-93

[6]

COUNTERION INDUCED PROCESSIBILITY OF CONDUCTING POLYANILINE [J].

CAO, Y ;

SMITH, P ;

HEEGER, AJ .

SYNTHETIC METALS, 1993, 57 (01) :3514-3519

[7]

Long-term anticorrosion behaviour of polyaniline on mild steel [J].

Chen, Y. ;

Wang, X. H. ;

Li, J. ;

Lu, J. L. ;

Wang, F. S. .

CORROSION SCIENCE, 2007, 49 (07) :3052-3063

[8]

Synthesis and electrical properties of polymer composites with polyaniline nanoparticles [J].

Cho, MS ;

Park, SY ;

Hwang, JY ;

Choi, HJ .

MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS, 2004, 24 (1-2) :15-18

[9]

Anticorrosion efficiency of organic coatings depending on the pigment volume concentration of polyaniline phosphate [J].

Kalendova, Andrea ;

Vesely, David ;

Sapurina, Irina ;

Stejskal, Jaroslav .

PROGRESS IN ORGANIC COATINGS, 2008, 63 (02) :228-237

[10]

Organic coatings containing polyaniline and inorganic pigments as corrosion inhibitors [J].

Kalendova, Andrea ;

Vesely, David ;

Stejskal, Jaroslav .

PROGRESS IN ORGANIC COATINGS, 2008, 62 (01) :105-116

← 1 2 →