Formation of an amorphous phase in thermally sprayed WC-Co

A WC-Co coating was sprayed by the high-velocity oxyfuel process using a feedstock of tungsten carbide clad with cobalt, The structure of the sprayed coating was characterized by x-ray diffraction (XRD), differential scanning calorimetry (DSC), and differential thermal analysis (DTA), It was found that an amorphous phase of Co-W-C ternary alloy observed as a large, broad peak in the XRD pattern can be formed in the as-sprayed WC-Co coating, The DSC, DTA, and XRD analyses revealed that the amorphous phase crystallized at a temperature of around 873 K to metallic cobalt, Co6W6C, and tungsten with appreciable precipitation of free carbon, The heat treatment of as-sp rayed WC-Co coating at a high temperature of 1173 K suggests that annealing at a temperature higher than about 1104 K will promote the reaction of tungsten and cobalt with carbon to form the complex carbide Co6W6C.